Polymer Property : Tensile Strength at Break = 7.00 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	7.00 MPa	1020 psi	ISO 37
PolyOne OnFlex™ S EH 80A-3S7005 Thermoplastic Elastomer (TPE) OnFlex™ S EH thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds are formulated to deliver a great cost/performance ratio in addition to t..
Tensile Strength at Break	7.00 MPa	1020 psi	ISO 37
PolyOne OnFlex™ S HF 90A-3S1988 Thermoplastic Elastomer (TPE) OnFlex™-S HF thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds utilize a unique, patent pending halogen free flame retardancy system. Fu..
Tensile Strength at Break	7.00 - 11.0 MPa	1020 - 1600 psi	ASTM D412
Proto3000 Objet Digital Materials™ DM_9130/9430/9230/9330 Rubber-like Prototyping Polymer Primary material: TangoBlackSecondary material: VeroWhitePlus, VeroBlue, VeroBlack, FullCure720Digital Materials are made up of two Objet materials. The two materials are combined in specific concen..
Tensile Strength at Break	>= 7.00 MPa	>= 1020 psi	DIN 53504
Huntsman AVALONÂ® 55 AEX Thermoplastic Polyurethane Introduction: AVALON 55 AEX is a high performance polyester based thermoplastic polyurethane for injection molding. AVALON 55 AEX is part of the AVALON Perform Range and offers a specially designed,..
Tensile Strength at Break	7.00 MPa	1020 psi	ASTM D638
ICO Polymers ICOTEXâ„¢ 520-5004 1000 Micron EVA Powder Description: ICOTEX 520-5004 is an EVA powder that has been developed to meet the special requirements of the textile coating industry. Key Characteristics: good melt flow and flexibility and a viny..
Tensile Strength at Break	7.00 MPa	1020 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL WCP761 PPE-TPE Flexible Noryl injection molding grade. Low specific gravity with very good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain re..
Tensile Strength at Break	7.00 MPa	1020 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL WCP761 PPE-TPE (Asia Pacific) Flexible Noryl injection molding grade. Low specific gravity with very good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain re..
Tensile Strength at Break	7.00 MPa	1020 psi	ISO 527
SABIC Innovative Plastics LNP STAT-LOY M3000 PP LNP STAT-LOY* M3000 is a compound based on unfilled Polypropylene resin. Added feature of this material is: Antistat.
Tensile Strength at Break	7.00 MPa	1020 psi	ISO 527-2
Total LDPE 1700 MN 18 C Low Density Polyethylene - Injection Molding and Compounding LDPE 1700 MN 18 C is a low density polyethylene made by a high pressure autoclave process without antioxidant. Grade for easy flow injection molding of flexible parts, powder production for grindin..
Tensile Strength at Break	7.00 MPa	1020 psi	ASTM D638
ELASTO UK Dryflex® 600650S SEBS Based Material, Filled Qualities, 65A Hardness, Natural The most significant features of the 600-series are the improved heat stability, the sound reduction and that the material enables an easy and secure pigmenting for the customer. A filled material ..
Tensile Strength at Break	7.00 MPa	1020 psi	ASTM D638
ELASTO UK Dryflex® 602600S SEBS Based Material, Filled Qualities, 60A Hardness, Black The most significant features of the 600-series are the improved heat stability, the sound reduction and that the material enables an easy and secure pigmenting for the customer. A filled material ..
Tensile Strength at Break	7.00 MPa	1020 psi	ASTM D638
ELASTO UK Dryflex® 602650S SEBS Based Material, Filled Qualities, 65A Hardness, Black The most significant features of the 600-series are the improved heat stability, the sound reduction and that the material enables an easy and secure pigmenting for the customer. A filled material ..
Tensile Strength at Break	7.00 MPa	1020 psi	ASTM D638
ELASTO UK Dryflex® 660600S SEBS Based Material, Semi-Filled Qualities, 60A Hardness, Natural The 660-series is recommended when the properties of the produced detail requires the advantages of the 500-series in combination with the 600-series. A semi-filled material can therefore combine t..
Tensile Strength at Break	7.00 MPa	1020 psi	ASTM D638
ELASTO UK Dryflex® 660650S SEBS Based Material, Semi-Filled Qualities, 65A Hardness, Natural The 660-series is recommended when the properties of the produced detail requires the advantages of the 500-series in combination with the 600-series. A semi-filled material can therefore combine t..
Tensile Strength at Break	7.00 MPa	1020 psi	ASTM D638
ELASTO UK Dryflex® 662650S SEBS Based Material, Semi-Filled Qualities, 65A Hardness, Black The 660-series is recommended when the properties of the produced detail requires the advantages of the 500-series in combination with the 600-series. A semi-filled material can therefore combine t..
Tensile Strength at Break	7.00 MPa	1020 psi	Across Flow; ASTM D412 and ISO 37
ExxonMobil Santoprene® 9101-80E Thermoplastic Vulcanizate - Co-extrusion Product Description: A black thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material is designed for coextrusion applications, particularly for the static foot of..
Tensile Strength at Break	7.00 MPa	1020 psi	ISO R 527
Fainplast Compounds GS 55/T Flexible PVC, Injection Molding for Footwear Soles
Tensile Strength at Break	7.00 - 10.0 MPa	1020 - 1450 psi	ISO 527-1
Adamas Adalon® 452 PTFE, Mica filler Information provided by Adamas, HPM
Tensile Strength at Break	7.00 MPa	1020 psi	ASTM D638
Azdel SuperLite® SL551400-100 PP Resin Matrix / 55% Glass Fiber (8 mm Molded Thickness) AZDEL SuperLite® SL551400-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic..
Tensile Strength at Break	7.00 MPa	1020 psi
Zelfo Technology Zelfo® HG Cellulose Fiber Material Zelfo® is a high performance bio-based material. Patented fibre technology developed by Zelfo Technology transforms 100% renewable or recycled cellulose fibres and water into self-binding Zelfo mat..