Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 191 PC (Asia Pacific) Nonhalogenated. 8.5 MFR. High impact. Thick wall sections. Opaques only. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® 193 PC Nonhalogenated. 8.5 MFR. High impact. Thick wall sections. UV-stabilized. Opaques only.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD1212 PC Copolymer 18 MFR LEXAN High Flow Ductile Copolymer |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD1212 PC Copolymer (Europe-Africa-Middle East) 18 MFR LEXAN High Flow Ductile Copolymer |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD1262 PC Copolymer (Asia Pacific) 19 MFR LEXAN High Flow Ductile Copolymerwith 400 nm cut off, available in transparent colors only |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® ML6412 PC Copolymer (Asia Pacific) ML6412 is an impact modified PC resin with non-brominated, non-chlorinated flame retardant system. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® EXRL0682 PC Copolymer 18 MFR LEXAN High Flow Ductile CopolymerThis data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HFD1212 PC Copolymer (Asia Pacific) 18 MFR LEXAN High Flow Ductile Copolymer |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
LG Chemical IF870S PMMA, General Purpose Grade for Injection Molding Highest flowability of all gradesFeatures: Excellent transparency and eleganceWeather resistance and chemical resistanceSurface hardness and coloring propertySuperior electrical resistance and mecha.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-20UV30 Polycarbonate, General Purpose, UV Stability Grade UV stability, Ultra Low viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Lighting covers, Safety products, E & E parts, Household applications, Leisure.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-30 Polycarbonate, General Purpose Features: Standard, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Lighting fixtures, Safety products, E & E parts, Household applications, Le.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-30FRT12 Polycarbonate, Flame Retardant Features: Non-brominated & non-chlorined flame retardant, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, E & E parts, Safety products, Househo.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-30UV Polycarbonate, General Purpose, UV Stability Grade Features: UV stability, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Lighting fixtures, Safety products, E & E parts, Household applications.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-40MRA Polycarbonate, General Purpose, Mold Release Grade Features: Mold release, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Lighting fixtures, Safety products, E & E parts, Household applications.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-40UV Polycarbonate, General Purpose, UV Stability Grade Features: UV stability, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Lighting fixtures, Safety products, E & E parts, Household applications.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-40UVR Polycarbonate, General Purpose, UV Stability + Mold Release Grade Features: UV stability, Mold release, Medium viscosityApplications: OA equipment, Communications, Precision parts, Machineries, Lighting fixtures, Safety products, E & E parts, Household application.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-50 Polycarbonate, General Purpose Features: Standard, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Lighting fixtures, Safety products, E & E parts, Household applications, Le.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
Kotec Carbotex K-50MRA Polycarbonate, General Purpose, Mold Release Grade Features: Mold release, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Lighting fixtures, Safety products, E & E parts, Household applications.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP IFL21 PA6.12 LNP LUBRICOMP* IFL21 is a compound based on Nylon 6/12 resin containing 5% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RP004 PA 66 (Asia Pacific) LNP* Lubricomp* RP004 is a compound based on Nylon 66 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics XYLEX HX7509HP PC+POLYESTER (Europe-Africa-Middle East) Medium flow, polycarbonate/Polyester alloy; contains mold release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), fo.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER PC+Polyester alloy. Houseware applications. USA/Europe Food contact. this grade will no longer be supported with biocompatibility information and should not be used for medical applications which r.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP KF002L Acetal Homopoly (Asia Pacific) LNP* Thermocomp* KF002L is a compound based on Acetal Homopolymer resin containing Glass Fiber. Added features of this material include: Low Extractible. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP KF002L Acetal Homopoly (Asia Pacific) LNP* Thermocomp* KF002L is a compound based on Acetal Homopolymer resin containing Glass Fiber. Added features of this material include: Low Extractible. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL NH7010 PPE+PS Noryl* NH7010 resin is a modified PPE-PS blend that exhibits an excellent balance of non-halogenated flame retardance, high heat resistance, good flow, and low specifc gravity for light weight parts.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Xylex FXY391DF PC+POLYESTER (Asia Pacific) PC+Polyester alloy in Diffusion Visual fx. This grade is compliant with US FDA/European food contact regulations. Color package may influence performance.This data was supplied by SABIC-IP for the A.. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Xylex X7529OQ PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Good flow with good impact and excellent optical qualityThis data was supplied by SABIC-IP for the Europe-Africa-Middle East r.. |
|||
Tensile Strength at Break | >= 63.0 MPa | >= 9140 psi | ASTM D638 |
UBE UBESTA® 3030UFX1 Rigid Industrial Grade Nylon 12 Description: UBE UBESTA® Industrial grade Nylon 12Comments: UV resistance, heat resistanceInformation provided by UBE. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | ISO 527-1/2 |
PTS POM-270 Acetal Copolymer Information provided by PTS LLC. |
|||
Tensile Strength at Break | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Xylex FXY391DF PC+POLYESTER (Europe-Africa-Middle East) PC+Polyester alloy in Diffusion Visual fx. This grade is compliant with US FDA/European food contact regulations. Color package may influence performance.This data was supplied by SABIC-IP for the E.. |