Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 4.50 MPa | 653 psi | ISO 37 |
PolyOne OnFlex™ S FR 40A-3S1841 Thermoplastic Elastomer (TPE) OnFlex™-S FR thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds are specially flame retarded with a highly effective, RoHS compliant halo.. |
|||
Tensile Strength at Break | 4.50 MPa | 653 psi | ISO 37 |
PolyOne OnFlex™ S KA 60A-3S1769 Thermoplastic Elastomer (TPE) OnFlex™-S KA thermoplastic elastomer compounds are based on hydrogenated styrenic block copolymers. This range of compounds are specially compatabilized to provide excellent adhesion to polyamide p.. |
|||
Tensile Strength at Break | <= 4.50 MPa | <= 653 psi | ISO/R527 |
Polykemi AB POLYelast TPE Z406 Thermoplastic Elastomer, SEBS-based Information provided by Polykemi AB |
|||
Tensile Strength at Break | 4.50 MPa | 653 psi | ISO R 527 |
Stir SpA IN 3341 AFCZ/X (PVC) Application: Extrusion flame resistant ecological fillerInformation provided by STIR SpA |
|||
Tensile Strength at Break | 4.50 MPa | 653 psi | ISO 527 |
A. Schulman INVISION™ VX-5065UI Soft Touch Polyolefin Thermoplastic ApplicationInvision™ VX-5065UI is targeted for automotive injection molding appearance applications. Information provided by A. Schulman. |
|||
Tensile Strength at Break | 4.50 - 6.00 MPa | 653 - 870 psi | DIN 53504 S2 |
Wacker Silicones Geniomer® 140 Silicone TPE SLM TPSE 140 is a silicone copolymer containing over 90% siloxane. Geniomer® is a two phase block copolymer made up of a soft polydimethylsiloxane (PDSM) phase and a hard aliphatic isocyanate phas.. |
|||
Tensile Strength at Break | 4.50 MPa | 653 psi | ISO 527 |
A. Schulman INVISION™ VX-5065UI Soft Touch Polyolefin Thermoplastic ApplicationInvision™ VX-5065UI is targeted for automotive injection molding appearance applications. Information provided by A. Schulman. |
|||
Tensile Strength at Break | 4.50 MPa | 653 psi | ISO 527 |
A. Schulman INVISION™ VX-5065UI Soft Touch Polyolefin Thermoplastic ApplicationInvision™ VX-5065UI is targeted for automotive injection molding appearance applications. Information provided by A. Schulman. |
|||
Tensile Strength at Break | 4.50 MPa | 653 psi | ISO 527 |
A. Schulman INVISION™ VX-5065UI Soft Touch Polyolefin Thermoplastic ApplicationInvision™ VX-5065UI is targeted for automotive injection molding appearance applications. Information provided by A. Schulman. |
|||
Tensile Strength at Break | 4.50 MPa | 653 psi | Across Flow; ASTM D412 |
ExxonMobil Santoprene® 8271-55 Thermoplastic Elastomer A soft, colorable, specialty, non-hygroscopic thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It complies with FDA regulations for rubber articles intended for repeated .. |
|||
Tensile Strength at Break | 4.50 MPa | 653 psi | ASTM D638 |
Arkema Group OREVAC® 9305 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |
|||
Tensile Strength at Break | 4.50 MPa | 653 psi | ASTM D412 |
Aearo E-A-R Specialty Composites VersaDamp™ V-2590 TPE VersaDamp TPEs are olefinic dynamic vulcanizates. The VersaDamp 2000 series materials provide predictable damping performance throughout a broad range of temperatures. They can be injection molded.. |
|||
Tensile Strength at Break | 4.50 MPa | 653 psi | ISO 527-1 |
Barlog Plastics KEBAFLEX E 55.1 TPE-V, Shore A55 TPE-VInformation provided by BARLOG plastics GmbH. |
|||
Tensile Strength at Break | 4.50 MPa | 653 psi | ISO 527-1 |
Barlog Plastics KEBAFLEX S 45 A.01 TPE-S, Shore A45, translucent TPE-SInformation provided by BARLOG plastics GmbH. |