Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 28.0 MPa | 4060 psi | STN EN ISO 527-2 |
Plastcom SLOVALEN PC 78 FRD 1 Polypropylene Copolymer, Halogen Flame Retardant, UV Stabilized FeaturesModified copolymer PP with the possibility of changing the MFI within the interval 5 - 20 g/10min. Stabilized against the UV-radiation by the UV stabilizer on the HALS basis. Retarded with.. |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycolac® EX39F ABS Highest impact extrusion ABS for sheet and blow molding applications. FDA food contact compliant. |
|||
Tensile Strength at Break | <= 28.0 MPa | <= 4060 psi | ISO/R527 |
Polykemi AB POLYfill PPH K20020 D Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 28.0 MPa | <= 4060 psi | ISO/R527 |
Polykemi AB POLYfill PPH TS15040 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | ISO 527 |
Eastman Eastar GN002 Copolyester, Natural
(discontinued **) Eastar GN002 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN002 copolyester will not crystallize and thus offers wider processing latitude tha.. |
|||
Tensile Strength at Break | <= 28.0 MPa | <= 4060 psi | ISO/R527 |
Polykemi AB POLYfill PP HIP8040 VT2 Polypropylene, Mineral Reinforced, Heat Resistant Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 28.0 MPa | <= 4060 psi | ISO/R527 |
Polykemi AB POLYfill PPH FR15030 XNH Polypropylene Homopolymer, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 28.0 MPa | <= 4060 psi | ISO/R527 |
Polykemi AB POLYfill PPH K20020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
Braskem BT 003 HDPE Blow Molding Polyethylene
(discontinued **) Applications: Bottles for food products, lubricating and cooking oil; toys; bottler for surface-active agents; sheets. Information provided by Braskem |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | ISO 12086 |
3M Dyneon™ TF 2021 PTFE
(discontinued **) Processable by standard paste extrusion methodsBoth grades can be processed at low to medium reduction ratiosTF 2021 PTFE is preferred for unsintered thread sealing tapes and expanded joint sealants.. |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | ISO 527 |
FKuR Kunststoff Bio-Flex® S 6540 Compostable PLA Blend The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta.. |
|||
Tensile Strength at Break | 28.0 - 35.0 MPa | 4060 - 5080 psi | ASTM D638 |
Manifattura Cattaneo PTFE Polytetrafluoroethylene Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
Tensile Strength at Break | 28.0 - 90.0 MPa | 4060 - 13100 psi | ASTM D683 |
Loxim 811 02T HB Polypropylene Compound, 10% Talc Filled, Flame Retardant Information provided by Loxim Industries |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCV063 PPE+SEBS+Polyolefin Flexible, non-halogenated FR, mPPE extrusion grade material for evaluation in automotive wire coating applications requiring ISO6722. |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP MB006HS PP (Asia Pacific) LNP* Thermocomp* MB006HS is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | 100mm/min, 4mm injection molded, unannealed; ISO 527-2 |
Styron EMERGEâ„¢ 5100 Acrylonitrile Butadiene Styrene (ABS) EMERGEâ„¢ ABS 5100 is a pre-colored, white, ABS resin, having high opacity and excellent toughness intended for manufacture of laser-marketable injection-molded smart cards.Information provided b.. |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | 50mm/min; ISO 527 |
Borealis Borstar® LE8706 Natural Bimodal LLDPE Jacketing Compound for Energy and Communication Cables Borstar® LE8706 is a natural colorable linear low density (LLD) jacketing compound, which is produced with the Borealis proprietary Borstar® bimodal process technology. Borstar technology allows .. |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | ISO 527-2 |
Tisan TISOPLEN® 10% Talc Filled Heat Stabilized Copolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | 50mm/min; ISO 527-2 |
Denka TE-30 Transparent Resin Polymer (MABS resin) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | ISO 527 |
Ecomass® 705ZC75 Stainless Steel Filled ABS Nontoxic Alternative to traditional metals, weighting and balancing applicationsModerate Specific GravityStainless Steel Powder Filled ABSInformation provided by Technical Polymers |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
Braskem GM5340PR High Density Polyethylene Triple-layer coating for metallic pipes; Umbilical pipes for offshore oil field platforms; Jacketing for wires and for optic fiber metallic cables; Self-propelled irrigation pipes; Localized irrigat.. |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0334M40CL Mica Reinforced Coupled |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339W40L Wollastonite Reinforced |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | ISO R 527 |
Addiplast Addilene J 310 Polypropylene Copolymer UnreinforcedInformation provided by Addiplast. |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | ASM D638 |
Bulk Molding Compounds BMC 940 Vinyl Ester Bipolar Plate Material Product Introduction: Bulk Molding Compounds, Inc. is the largest manufacturer of thermoset bulk molding compounds in North America, serving the automotive, appliance, and electrical markets. BMC t.. |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339M30L Mica Reinforced |
|||
Tensile Strength at Break | <= 28.0 MPa | <= 4060 psi | ISO/R527 |
Polykemi AB POLYfill PPH TS3020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 28.0 MPa | 4060 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics SABIC PPCOMPOUND 15T1040 PP SABIC® PPcompound 15T1040 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound, suitable for injection molding applications. The IMDS ID is 16487994 |
|||
Tensile Strength at Break | 28.0 MPa @Temperature 23.0 °C |
4060 psi @Temperature 73.4 °F |
ISO 527 (1BA bar) |
DuPont Performance Polymers Hytrel® 4068FG TPC-ET
(Unverified Data**) Hytrel® 4068FG is a high performance thermoplastic polyester elastomer with food compliance specificity.Information provided by DuPont Performance Polymers |