Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 24.1 MPa | 3500 psi | 2 in/min; ASTM D638 |
RheTech Products CC40P100-00EG 40% Calcium Carbonate Reinforced Polypropylene, Natural, Extrusion Grade Applications: Consumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | 2 in/min; ASTM D638 |
RheTech Products M25UVP250-01 25% Mica Reinforced Polypropylene Copolymer, UV Stabilized, Black Applications: BracketsCowl screensRigid exterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | >= 24.1 MPa | >= 3500 psi | ASTM D638 |
Niche Polymer PPCM15BK Copolymer PP Information provided by Niche Polymer |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 90046 Polyvinyl Chloride, Flexible (PVC, Flexible) Automotive OEM approval(s).Information provided by PolyOne |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
ExxonMobil HD 9856BA Blow Molding Resin
(discontinued **) HD 9856BA is a HDPE blow molding resin designed for high performance packaging applications. Containers made from HD 9856BA exhibit a unique combination of stiffness and environmental stress cracki.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 16% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
LyondellBasell Alathon® M5370WC High Density Polyethylene ApplicationsALATHON M 5370WC is a natural, high density, polyethylene copolymer resin with a narrow molecular weight distribution formulated for use as primary insulation for coaxial and control cab.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D1414 |
Greene Tweed FLUORAZ® 790 Fluoroelastomer, FEPM Greene, Tweed`s Fluoraz® functions effortlessly in a variety of challenging process environments. Fluoraz performs well in aggressive chemicals where ultrapure materials are not required. Known f.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D412 |
ITW Devcon Flexane® Rubber Repair / Castable Urethane Brushable, Black Information provided by ITW Devcon |
|||
Tensile Strength at Break | 24.1 - 26.2 MPa | 3500 - 3800 psi | |
ITW Plexus Plexusâ„¢ MA822 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Designed for structural bonding of metals without primers.Information provided by Illinois Tool Wo.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
Teknor Apex APEX® 80862 Polyvinyl Chloride, Semi-Rigid Notes: 105°C Insulation; RoHS Compliant Features: High Heat Resistance; Semi-rigid Uses: Cable Jacketing; Insulation Agency Ratings: UL 1061 Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
Teknor Apex APEX® 80862-F Polyvinyl Chloride, Flexible Notes: 105°C Insulation; RoHS Compliant Uses: Wire and Cable Applications Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | at max load; ASTM D638 |
A. Schulman PP 1277A-01 Polypropylene High-Impact Polypropylene DescriptionPolypropylene PP 1277A is a low-flow, high-impact polypropylene for film, profile, tubing and coating.Information provided by A. Schulman. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D412 |
Teknor Apex Telcar® TL-2683B Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | at max load; ASTM D638 |
A. Schulman PP 1277A-01 Polypropylene High-Impact Polypropylene DescriptionPolypropylene PP 1277A is a low-flow, high-impact polypropylene for film, profile, tubing and coating.Information provided by A. Schulman. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | at max load; ASTM D638 |
A. Schulman PP 1277A-01 Polypropylene High-Impact Polypropylene DescriptionPolypropylene PP 1277A is a low-flow, high-impact polypropylene for film, profile, tubing and coating.Information provided by A. Schulman. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
Westlake Plastics HIPS High Impact Polystyrene, Compression Molded Compression molded HIPS is a low cost plastic material that is easily machined and fabricated. It is frequently used for preproduction prototyping. HIPS is a FDA compliant use in food processing a.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | at max load; ASTM D638 |
A. Schulman PP 1277A-01 Polypropylene High-Impact Polypropylene DescriptionPolypropylene PP 1277A is a low-flow, high-impact polypropylene for film, profile, tubing and coating.Information provided by A. Schulman. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
Westlake Plastics HIPS High Impact Polystyrene HIPS is a low cost plastic material that is easy to machine and fabricate. It is often specified for low strength structural applications when impact resistance, machinability, and low cost are req.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D3759 |
3M 4H83C Protective Laser Tape 3M™ Protective Laser Tape 4H83 is a clear or white multi-polymer film coated with medium-tack adhesive designed especially to help provide temporary protection of #3 & #4 stainless steel sheets dur.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 16% Plasticizer
(discontinued **) Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D412 |
DuPont Performance Polymers Kalrez® 3065 Fluoroelastomer DuPont™ Kalrez® 3065 is a highly-filled product containing carbon black and fiber reinforcement, designed to function without extrusion under extreme pressure. It has good all round chemical resis.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable W1349L-xx05FRD Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | TM R050-36 |
Resinlab® EP1046FG Black Electronic Grade Epoxy Encapsulant Resinlab™ EP1046FG Black is a two part unfilled very fast curing electronic grade epoxy encapsulant designed for small castings (less than 25 grams). It cures very quickly with low exotherm to a to.. |
|||
Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D638 |
PlastxWorld DAICEL STYROL® GW50 HIPS UV stable flame retarded HIPSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |