Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 159 MPa | 23000 psi | ASTM D638 |
Oxford Polymers 40GF 40% Glass Fiber Filled Polycarbonate for Injection Molding 40% Glass Fiber Filled Polycarbonate for Injection MoldingInformation provided by Oxford Polymers. |
|||
Tensile Strength at Break | 159 MPa | 23000 psi | ASTM D638 |
Oxford Polymers PEEK 20GF-Natural PEEK, 20% Glass Fiber Reinforced Product Description: Glass Fiber (20% Reinforced), PEEK, Polyetheretherketone injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Glass fiber Special Chara.. |
|||
Tensile Strength at Break | 159 MPa | 23000 psi | ASTM D638 |
Polymer Resources NY66-FRG25 Flame Retardant Nylon 66, 25% Glass Reinforced Nylon 66, 25% Glass Reinforced, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are.. |
|||
Tensile Strength at Break | 159 MPa | 23000 psi | 73°F; ASTM D638 |
Ravago Manufacturing Americas Hylon® N1025HLFR Nylon 6/6 (DAM)
(discontinued **) Information provided by Ravago. |
|||
Tensile Strength at Break | 159 MPa | 23100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36S PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFL36S is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 159 MPa | 23100 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON PFD06 PA 6 (Asia Pacific) LNP* Stat-kon* PFD06 is a compound based on Nylon 6 resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 159 MPa | 23000 psi | ASTM D638 |
Techmer ES Plaslube® J-1/30/TF/15 RED PA66 |
|||
Tensile Strength at Break | 159 MPa | 23100 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RF004 PA 66 LNP THERMOCOMP* RF004 is a compound based on Nylon 66 resin containing 20% Glass Fiber. |
|||
Tensile Strength at Break | 159 MPa | 23100 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RF004XXD PA 66 LNP THERMOCOMP* RF004XXD is a compound based on Nylon 66 resin containing 20% Glass Fiber. |
|||
Tensile Strength at Break | 159 MPa | 23100 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF006S PA 66 LNP* THERMOCOMP* RF006S is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 159 MPa | 23100 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF006S PA 66 (Asia Pacific) LNP* Thermocomp* RF006S is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 159 MPa | 23100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP LF006E PEEK (Europe-Africa-Middle East) LNP* THERMOCOMP* LF006E is a compound based on Polyetheretherketone resin containing Glass Fiber. Added features include: Easy Molding. |
|||
Tensile Strength at Break | 159 MPa | 23000 psi | ASTM D638 |
A. Schulman SCHULADUR® A GF50 50% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
Tensile Strength at Break | 159 MPa | 23000 psi | ASTM D638 |
Techmer Lehvoss Compounds Luvotech™ J-1305/40 BK5011 PPS
(discontinued **) Techmer Lehvoss Compounds, a JV between Techmer ES and Lehmann&Voss&Co. has been terminated. |