Oxford Polymers 40GF 40% Glass Fiber Filled Polycarbonate for Injection Molding
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 40% Glass Filled |
| Manufacturer | Oxford Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Oxford Polymers 40GF 40% Glass Fiber Filled Polycarbonate for Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40% Glass Fiber Filled Polycarbonate for Injection MoldingInformation provided by Oxford Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Filler Content | 40 % | 40 % | |
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 159 MPa | 23000 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 11.6 GPa | 1680 ksi | ASTM D638 |
| Flexural Strength | 186 MPa | 27000 psi | ASTM D790 |
| Flexural Modulus | 9.65 GPa | 1400 ksi | ASTM D790 |
| Compressive Strength | 145 MPa | 21000 psi | ASTM D695 |
| Izod Impact, Notched | 0.961 J/cm @Temperature 23.0 °C |
1.80 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 293 °C | 560 °F | |
| Back Pressure | 103 MPa | 15000 psi | Mold pressure |
Users viewing this material also viewed the following:
- SABIC PS 160 General Purpose Polystyrene for Foam Extrusion
- Premix Premi-Glas® 2203-22 CR-SX-HT Fiberglass Reinforced Thermoset SMC
- Permabond CSA Cyanoacrylate Surface Activator
- Lubrizol Advanced Materials PEARLTHANE® 11T65D Thermoplastic Polyurethane Elastomer
- Supreme Petrochem SH 2114 High Impact Polystyrene
- Plastics Group Polifil® 71MR Mineral-Reinforced Nylon 6/6 (DAM)
- Tra-Con Tra-Bond 2162D Color Coded Smooth Paste Epoxy Adhesive
- ExxonMobil Mobil Velocite 4
- Fainplast Compounds PH 75 Flexible PVC, Transparent Extrusion
- Carpenter Gall-Tough PLUS™ Stainless, Annealed
Copyright © lookpolymers.com All Rights Reserved