Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable JJC32A Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | 2 in/min; ASTM D638 |
RheTech Products FT4200-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Body side moldingsGrillesElectrical housingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | 2 in/min; ASTM D638 |
RheTech Products FT4200-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Body side moldingsGrillesElectrical housingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | |
NEU NeuSoft™ 596-50A Medical Ether TPU / SBC blend |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible FC900 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible XV 3450 Polyvinyl Chloride, Flexible (PVC, Flexible) NOTE: All ingredients used in the formulation of this compound are listed in the United States FDA Code of Federal Regulations, Title 21. The only restriction is that the plasticizer is For foods of.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ HC 2170 Polyvinyl Chloride, Flexible (PVC, Flexible) Geon HC 2170 is a 70 Shore A non-phthalate flexible vinyl compound made from FDA sanctioned ingredients. HC 2170 can be used for extrusion and injection molding healthcare applications.NOTE: All ing.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible B4DC1 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible F80E Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R252BE Polyvinyl Chloride + NBR (PVC+NBR) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R312AE Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R336AE Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible R352AE Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | 50 mm/min; ASTM D638 |
LyondellBasell Alathon® M6080 High Density Polyethylene, Injection Molding Grade ALATHON M6080 is a narrow molecular weight distribution homopolymer that exhibits enhanced flow characteristics and good balance of stiffness and impact resistance. Typical applications include case.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | ISO R 527 |
Stir SpA AF 80 3 IK (PVC) Application: Insulation CEI 20-11 type R 2 low acid fumes emissionInformation provided by STIR SpA |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | ASTM D638 |
Teknor Apex APEX® 3610-75 Polyvinyl Chloride, Flexible Uses: Medical/Healthcare Applications Agency Ratings: NSF 61 Forms: Pellets Additional Information: First Generation SeriesInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | ASTM D638 |
Teknor Apex APEX® 4167 Polyvinyl Chloride, Flexible Notes: 60°C Jacket; RoHS Compliant Features: High Gloss; Sunlight Resistant (720 hours)Uses: Flexible Cord Jacketing Forms: Pellets Wire Types: SJTW; STW; SJT; SRDT; ST; SVT Agency Ratings: UL QM.. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | ASTM D638 |
Teknor Apex APEX® 94-A1235-C-75-NT1 Polyvinyl Chloride, Flexible Notes: RoHS Compliant Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | ASTM D412 |
Teknor Apex Monprene® MP 1061 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | >= 15.9 MPa | >= 2300 psi | ASTM D412 Method A |
Seals Eastern 7182A Fluorocarbon-Elastomer Formulated AFLAS® high-temperature, high-pressure "sour" oil & gas service. Resistant to extrusion. Excellent acid and base resistance.Information provided by Seals Eastern, Inc. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | ISO R 527 |
Stir SpA Z 74 AT 1 (PVC) Application: Molding for beach footwearInformation provided by STIR SpA |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | ASTM D638 |
Westlake Plastics TPX® Polymethylpentene TPX is a lightweight, high temperature polyolefin with exceptional acoustical and electrical properties. TPX has low moisture absorption and excellent chemical resistance. It is often used for app.. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | |
Abatron ROCKWELD 55-27 A/B Structural Adhesive Putty; Epoxy ROCKWELD 55-27 is a 2-component epoxy system with low density, high-strength, and no shrinkage. It is a structural adhesive putty for sculpturing, repairs and restoration of stone, concrete and maso.. |
|||
Tensile Strength at Break | 15.9 MPa | 2310 psi | Press Cure 10 Minutes @ 188°C, Post Cure 16 Hours @ 250°C |
3M Dyneon™ 131TZ High Temperature Perfluoroelastomer 3M™ Dyneon™ 131TZ is a technically advanced high temperature perfluoroelastomer (HT PFE). It is designed to meet the challenges of higher temperature applications. It is classified as FFKM per AST.. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FE 5623 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FE 5623 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul.. |
|||
Tensile Strength at Break | 15.9 MPa | 2300 psi | ASTM D638 |
ExxonMobil Paxon™ AA50-002 Blow Molding Resin
(discontinued **) AA50-002 is a blow molding grade high density polyethylene. This resin has excellent stress crack resistance combined with high impact strength, rigidity, and melt strength.Information provided by .. |