Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 148 MPa | 21500 psi | ASTM D638 |
Polymer Resources PPX/NY G30 PPO/Nylon 66 Alloy , 30% Glass Reinforced Polyphenylene Oxide/Nylon 66 Alloy , 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informa.. |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DFL28 PC (Asia Pacific) LNP* Lubricomp* DFL28 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | ASTM D638 |
Ravago Manufacturing Americas Enviramid™ N2335HL BK Nylon 6 Available in North America Filler: Glass Fiber Reinforcement, 35% Filler by WeightAdditive: Heat Stabilizer and Lubricant Features: Lubricated and Heat StabilizedContains Recycled ContentRoHS Compl.. |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFP36 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFP36 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone. |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM SF2260 PEI Blend (Asia Pacific) High flow Ultem for thin wall application |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM SF2360 PEI Blend (Asia Pacific) High flow Ultem for thin wall application |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DX13320C PC COPOLYMER (Asia Pacific) LNP* Statkon DX13320C is ultra clean polycarbonate/carbon fiber compound with high modulus, good flow ability, easy mold release, and high level of cleanliness for the most demanding application. A .. |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RF004XXH PA 66 LNP THERMOCOMP* RF004XXH is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DE006ER PC LNP STAT-KON* DE006ER is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Easy Molding. Mold Release, Electrically Conductive. |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | ISO 527 |
SABIC Innovative Plastics LNP Thermocomp DF008P PC (Asia Pacific) LNP* THERMOCOMP* DF008P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the.. |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | ASTM D638 |
Chase Plastics CP Pryme® NN130M2 (Dry) Nylon 66, 30% Glass Fiber Reinforced, Lubricated Features: Good chemical resistanceGood compressive strengthGood creep resistanceFast cycleLubricatedHigh rigiditySolvent resistanceHigh strengthForm: PelletsInformation provided by Chase Plastics. |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | ASTM D638 |
Chase Plastics CP Pryme® NN130M2HS (Dry) Nylon 66, 30% Glass Fiber Reinforced, Lubricated, Heat Stabilized Features: Good chemical resistanceGood compressive strengthGood creep resistanceFast cycleHeat stabilizedLubricatedHigh rigiditySolvent resistanceHigh strengthForm: PelletsInformation provided by Ch.. |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | DAM; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® 80G33HS1L BK104 Nylon 66
(Unverified Data**) 33% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 80G33HS1L BK104 is a 33% glass fiber reinforced heat stabilized black polyamide 66 resin with outstanding impact resistance develope.. |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GF 1800 33 BLACK 13 Nylon 612 with 33% Glass Fiber
(discontinued **) Molded Test Bars: Dry as Molded |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | ISO 527-1 |
Vyncolit Neopreg Kinel® SK4504 S12 Carbon Reinforced Molding Compound Epoxy based molding compound long carbon fiber reinforced suited for demanding tribologic applications under dry running conditions, exposed to a wide range of temperatures (-100°C up to 150°C)... |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | ASTM D638 |
Polymer Resources PPX/NY G30 Modified PPO, 30% Glass Reinforced PPX/Nylon 6,6 Alloy
(Unverified Data**)&l Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength at Break | 148 MPa | 21500 psi | ISO 527-1/-2 |
DuPont Performance Polymers Crastin® SK695FR BK507 Polybutylene Terephthalate (PBT)
(Unverified Data**)&l 30% Glass Reinforced Flame Retardant Polybutylene Terephthalate Crastin® SK695FR is a 30% glass reinforced flame retardant polybutylene terephthalate for injection moulding.Information provided b.. |