Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 12.4 MPa | 1800 psi | 510 mm/min; ASTM D412A |
PolyOne Elastamax™ XL-1035-21-8001 Black Styrene Butadiene Block Copolymer (SBC) A thermoplastic elastomer compound formulated for use in food contact applications. The physical properties listed above are typical values obtained on laboratory prepared samples and tested in acco.. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne FireCon™ CPE 37-11 RoHS BLACK Polyethylene, Chlorinated (CPE) CPE-37-11 RoHS BLACK is a heavy duty thermoplastic jacket for power and control cables. It is suitable for VW1 and tray fire rated applications. CPE-37-11 RoHS BLACK offers the highest physical prop.. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible 90212 Polyvinyl Chloride, Flexible (PVC, Flexible) Provisional Product Information - Physical and Mechanical properties based on initial production.Information provided by PolyOne |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D638 |
Resirene Resirene® READ 9500 Ignition Resistant Impact Polystyrene Features:High FlowIgnition ResistantNo Pre-drying RequiredHigh ImpactColors AvailableApplications:Injection MoldingDark ColorsTV CabinetsElectronic EquipmentInformation provided by US distributor Ca.. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ HC 2160G Polyvinyl Chloride, Flexible (PVC, Flexible) Geon HC 2160G is a 60 Shore A non-phthalate, gamma-stable flexible vinyl compound made from FDA sanctioned ingredients. HC 2160G can be used for extrusion and injection molding healthcare applicatio.. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D638 |
LyondellBasell Microthene® F FN51000 Low Density Polyethylene General DescriptionMicrothene F polyolefin powders are ultra-fine, spherically shaped particles with narrow size distribution suitable for use in a broad range of specialty applications. Microthene.. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D638 |
LyondellBasell Microthene® F FN51900 Low Density Polyethylene General DescriptionMicrothene F polyolefin powders are ultra-fine, spherically shaped particles with narrow size distribution suitable for use in a broad range of specialty applications. Microthene.. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D638 |
LyondellBasell Petrothene® NA217080 Low Density Polyethylene ApplicationsPETROTHENE NA 217-080 is a natural low density polyethylene resin formulated for use as primary insulation for coaxial and control cable applications. NA 217-080 has also been designed .. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D638 |
Manifattura Cattaneo RULON® W2 Polytetrafluoroethylene Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | |
Indium Corp. Indalloy 170 Pure Lead Information Provided by Indium Corporation |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ISO R 527 |
Stir SpA FB 57 S (PVC) Application: Extrusion glossy cableInformation provided by STIR SpA |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D412 |
Teknor Apex Monprene® MP-2318 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D412 |
Teknor Apex Monprene® MP-2327-R Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D412 |
Teknor Apex APEX® 2065-H Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMFeatures-Good FlexibilityUses-General Purpose, ProfilesAppearance-ClearForms-PelletsProcessing Method-Extrusi.. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D412 |
Sumitomo Chemical ESPOLEX® UT461A Thermoplastic Elastomer ESPOLEX® TPE Series is a group of thermoplastic elastomers produced by Sumitomo Chemical Company. Among its material advantages, ESPOLEX® TPE Series is distinguished by offering many low-densi.. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D412 |
Teknor Apex Telcar® TL-1996E Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D412 |
Teknor Apex Telcar® TL-8730R Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ISO 37 |
Alliance Polymers Viprene™ G90A-32U-BLK Thermoplastic Vulcanizate Elastomer Viprene™ G90A-32U-BLK is a UV and Heat Stabilized TVP (Thermoplastic Vulcanizate Elastomer). This material can be easily processed by extrusion or injection molding. It exhibits easy flowing charac.. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ISO 37 |
Alliance Polymers Viprene™ G90A-32U-NAT Thermoplastic Vulcanizate Elastomer Viprene™ G90A-32U-NAT is a UV and Heat Stabilized TVP (Thermoplastic Vulcanizate Elastomer). This material can be easily processed by extrusion or injection molding. It exhibits easy flowing charac.. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FX 11818 Fluoroelastomer 3M™ Dyneon™ Flouroelastomer FX 11818 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
Tensile Strength at Break | 12.4 - 15.2 MPa | 1800 - 2200 psi | ASTM 638-01 |
3M 32660 Heavy Duty Performance Coating - Part A 3M™ HD (Heavy Duty) Performance Coating is 100% solids elastomeric lining especially developed for high abrasion and tear resistance with thick build up characteristics. It has good durability and .. |
|||
Tensile Strength at Break | 12.4 - 15.2 MPa | 1800 - 2200 psi | ASTM 638-01 |
3M 32665 Green Heavy Duty Performance Coating - Part B 3M™ HD (Heavy Duty) Performance Coating is 100% solids elastomeric lining especially developed for high abrasion and tear resistance with thick build up characteristics. It has good durability and .. |
|||
Tensile Strength at Break | 12.4 - 15.2 MPa | 1800 - 2200 psi | ASTM 638-01 |
3M 32666 Tan Heavy Duty Performance Coating - Part B 3M™ HD (Heavy Duty) Performance Coating is 100% solids elastomeric lining especially developed for high abrasion and tear resistance with thick build up characteristics. It has good durability and .. |
|||
Tensile Strength at Break | 12.4 - 15.2 MPa | 1800 - 2200 psi | ASTM 638-01 |
3M 32663 Medium Grey Heavy Duty Performance Coating - Part B 3M™ HD (Heavy Duty) Performance Coating is 100% solids elastomeric lining especially developed for high abrasion and tear resistance with thick build up characteristics. It has good durability and .. |
|||
Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D638 |
Resirene Resirene® 6110 High Impact Polystyrene Features:High ImpactEasy ProcessingFDA Rating: 21 CFR 177.1640FlexibilityApplications:Injection MoldingTV CabinetsRemote ControlsToysInformation provided by US distributor Calsak Corporation. |