Manifattura Cattaneo RULON® W2 Polytetrafluoroethylene
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo RULON® W2 Polytetrafluoroethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.10 g/cc | 0.0759 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.00 % @Temperature 23.0 °C |
0.00 % @Temperature 73.4 °F |
50% RH; ASTM D570 |
| Water Absorption at Saturation | 0.00 % | 0.00 % | ASTM D570 |
| Deformation | 3.0 % @Time 86400 sec, Pressure 100 MPa |
3.0 % @Time 24.0 hour, Pressure 14500 psi |
ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 60 | 60 | ASTM D 2240 |
| Tensile Strength at Break | 12.4 MPa | 1800 psi | ASTM D638 |
| Elongation at Break | 70 % | 70 % | ASTM D638 |
| Compressive Yield Strength | 5.90 - 6.20 MPa @Strain 1.00 %, Time 3.60e+6 sec |
856 - 899 psi @Strain 1.00 %, Time 1000 hour |
ASTM D695 |
| Compressive Modulus | 0.450 GPa | 65.3 ksi | ASTM D695 |
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | on polished steel; MPC Test |
| Coefficient of Friction, Static | 0.15 | 0.15 | on polished steel; MPC Test |
| K Factor (Wear Factor) | 0.10 | 0.10 | µm/s. PV = 0.1 MPa-m/s; max P = 6.9 MPa; MPC Test |
| Limiting Pressure Velocity | 0.350 MPa-m/sec | 9990 psi-ft/min | without lubrication; MPC Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 108 - 154 µm/m-°C @Temperature 23.0 - 100 °C |
60.0 - 85.6 µin/in-°F @Temperature 73.4 - 212 °F |
|
| CTE, linear, Transverse to Flow | 84.0 - 110 µm/m-°C @Temperature 23.0 °C |
46.7 - 61.1 µin/in-°F @Temperature 73.4 °F |
|
| Thermal Conductivity | 0.650 W/m-K | 4.51 BTU-in/hr-ft²-°F | ASTM D177 |
| Maximum Service Temperature, Air | 288 °C | 550 °F | |
| Minimum Service Temperature, Air | -240 °C | -400 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | No | No |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Dull Black | |
| UV Resistance | Y |
Users viewing this material also viewed the following:
- Quadrant EPP Proteus® LSG HS PP - Heat Stabilized Polypropylene (ASTM Product Data Sheet)
- Polymer Resources PC-FR3-D Polycarbonate, Improved Flame Retardant, High Flow
- Overview of materials for Nylon 66, Carbon Fiber/PTFE Filled
- Karina E 820-18/100-CR Gray PVC Compound
- A. Schulman POLYBATCH™ Gardenia P80515PF Concentrate Based In Polypropylene
- Westlake Plastics Radel® R 5500 Polyphenylsulfone
- Unitika elitel UE3800 Polyester, Pellet
- EMS-Grivory Grivory® AS LF 20 PA66-Z20
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 305, 50% Cold Rolled (UNS S30500)
- Fainplast Compounds KL 95/1 Flexible PVC, Insulation for High Temperatures Lead Free
Copyright © lookpolymers.com All Rights Reserved