Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Yield Strength | 138 MPa | 20000 psi | 10% Def.; ASTM D695 |
Quadrant EPP Ketron® CM HPV PEEK Polyetheretherketone; PTFE, Graphite, and Carbon Fiber Filled Bearing Grade, compression molded (ASTM Product Data Sheet) Excellent chemical resistance Very low moisture absorption Inherently good wear and abrasion resistance Unaffected by continuous exposure to hot water or steam |
|||
Compressive Yield Strength | 138 - 255 MPa | 20000 - 37000 psi | Average value: 179 MPa Grade Count:6 |
Overview of materials for Nylon 66, Glass/Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass/Mineral Filled". Each property range of values reported is minimum and maximum values of.. |
|||
Compressive Yield Strength | 138 MPa | 20000 psi | ASTM D256 |
Techmer ES Electrafil® J-1/CF/30/TF/15 Nylon 66, 30% Carbon Fiber Reinforced, PTFE Lubed Carbon Fiber Reinforced, PTFE Lubricated |
|||
Compressive Yield Strength | 138 MPa @Strain 1.00 % |
20000 psi @Strain 1.00 % |
ASTM D695 |
Saint-Gobain Fluoroloy® A22 High Performance Seal Material High modulus with excellent high-temperature resistance; Abrasion resistant; Chemically Inert; Recommended for back-up rings and for special applications.
Information provided by Saint-Gobain P.. |
|||
Compressive Yield Strength | 138 MPa | 20000 psi | at 8% compression |
Zircar Refractory Composites RS-DR Refractory Sheet TYPE RS-DR is a rigid pre-fired sheet that has been heat-treated to remove all organic binder and is stable to moisture attack. Refractory Sheet Type RS-DR is suited for use as a setter or barrier f.. |
|||
Compressive Yield Strength | 138 MPa | 20000 psi | ASTM D695 |
Adell BR-14 Nylon 6, 20% Glass Reinforced Data provided by Adell Plastics, Inc. |
|||
Compressive Yield Strength | 138 MPa | 20000 psi | ASTM D695 |
Adell BR-34 Nylon 6, 20% Glass Reinforced Data provided by Adell Plastics, Inc. |
|||
Compressive Yield Strength | 138 MPa | 20000 psi | ASTM D695 |
Adell AJ-14 Nylon 66, 20% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
Compressive Yield Strength | 138 MPa | 20000 psi | ASTM D695 |
Adell AJ-34 Nylon 66, 20% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
Compressive Yield Strength | 138 MPa | 20000 psi | Max load under tribological use |
Saint-Gobain Rulon® FCJ Grade Bearing/Seal PTFE
(discontinued **) Saint Gobain Rulon® CJ is now produced as a part of the TriStar Plastics Corp. product line under the CJ Bearings trade name.Description: Rulon® is the Saint-Gobain trade name for their family of .. |
|||
Compressive Yield Strength | 138 - 179 MPa | 20000 - 26000 psi | Average value: 153 MPa Grade Count:12 |
Overview of materials for Diallyl Phthalate (DAP), Cast, Mineral Filler This property data is a summary of similar materials in the MatWeb database for the category "Diallyl Phthalate (DAP), Cast, Mineral Filler". Each property range of values reported is minimum and ma.. |
|||
Compressive Yield Strength | 138 MPa | 20000 psi | ASTM D695 |
Sumitomo Bakelite North America RX® 1-510N Mineral Filled Diallyl Phthalate Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Information provided by Sumitomo Bak North Americ.. |