Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 62.0 MPa | 8990 psi | 2 mm/min; ASTM D 790 |
Polimeri Europa Sinkral® E 332 ABS Resin Sinkral E 332 is a medium heat injection molding grade offering good flow and good impact resistance together with an excellent thermal stability during processing. Designation: Thermoplastic ISO 2.. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP FARADEX KX88084 POM (Europe-Africa-Middle East) LNP* Faradex* KX88084 is a compound based on POM resin containing Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Europe-Africa-Middle East) LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | <= 62.0 MPa | <= 8990 psi | ISO 178 |
Polykemi AB POLYfill PPH T4060 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP ABL12 ABS LNP* Lubricomp* ABL12 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% Glass Bead and 5% PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS (Europe-Africa-Middle East) LNP* LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Asia Pacific) LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP AL004 ABS LNP* Lubricomp* AL004 is a compound based on Acrylonitrile Butadiene Styrene resin containing 20% PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
IDI Composites 46-3 Thermoset Polyester, Molding Superior electrical performance with low pressure molding for V-O flammability in encapsulation applications.Data provided by the manufacturer. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | 5 mm/min; ISO 178 |
Gromax BTE65-DN001N1 Nylon 6 (Dry) Information provided by Gromax Enterprises Corp. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP HH0420A PA11 LNP* HH0420A is a compound based on Nylon 11 containing proprietary fillers. Added features of this material are High Specific Gravity. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KX06415 Acetal Copolymer LNP LUBRICOMP* KX06415 is a compound based on Acetal Copolymer resin containing 10% PTFE, 10% Aramid Powder. Added features of this material include: Easy Molding, Heat Stabilized, Wear Resistant. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | 2 mm/min; ISO 178 |
Styrolution Novodur® P2M-AT ABS Pellets Novodur® P2M-AT has high impact strength, high gloss, and contains antistatic additive. It is used for the production of molded plastic articles. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ISO Data |
Styrolution Terblend® N NM-19 ABS/PA6 (Dry) Terblend N NM-19 is a UV stabilized ABS/PA6 blend combining very high impact strength, even at low temperatures with an excellent processability and surface appearance.Information provided by STYROL.. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp WH0500B PBT LNP* THERMOCOMP* WH0500B is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.This data was .. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007F Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007F is a 40% talc filled homopolymer polypropylene compound that utilizes FDA compliant raw materials.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1310 Coupled Mica Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1310 is a Coupled Mica filled homopolymer polypropylene compound for injection molding.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
Unitika EX-1222 PA6, Dry High-impact nylonInformation provided by Unitika Ltd. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007E is a 40% talc filled homopolymer compound for extrusion applications.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007F Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007F is a 40% talc filled homopolymer polypropylene compound that utilizes FDA compliant raw materials.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007 is a 40% talc filled homopolymer polypropylene compound.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007F Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007F is a 40% talc filled homopolymer polypropylene compound that utilizes FDA compliant raw materials.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007E is a 40% talc filled homopolymer compound for extrusion applications.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
Denka CL-430 Transparent Resin Polymer (MABS) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ISO 178 |
Eurostar Star L POM D84 POM, Injection Molded Star L POM D84 is a PTFE/Proprietary Additive Lubricated, POM Copolymer Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | 2 mm/min; ISO 178 |
Chi Mei Polyrex® PG-33 Polystyrene Standard grade |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
Aclo Accucomp ABS ABS846HL High Flow Medium Impact Grade |
|||
Flexural Strength | <= 62.0 MPa | <= 8990 psi | ISO 178 |
Polykemi AB POLYfill PPH T5060 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Strength | 62.0 MPa | 8990 psi | ASTM D790 |
A. Schulman POLYFLAM™ FPP 1007 Talc Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1007 is a 40% talc filled homopolymer polypropylene compound.Information provided by A. Schulman. |
|||
Flexural Strength | 62.0 MPa | 8990 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON KEL32 Acetal Copolymer (Europe-Africa-Middle East) LNP* LUBRICOMP* KEL32 is a compound based on Acetal Copolymer resin containing Carbon Fiber, PTFE. Added features include: Electrically Conductive, Internally Lubricated. |