Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 77.7 MPa | 11300 psi | ASTM D790 |
PolyOne Geon™ Vinyl Packaging 2798 Polyvinyl Chloride, Rigid (PVC, Rigid) Premium chemical resistant Compound for Packaging.Information provided by PolyOne |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
PolyOne Geon™ Vinyl Packaging PK8-1080 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Flexural Strength | 77.9 MPa | 11300 psi | ASTM D790 |
PolyOne Geon™ Vinyl Rigid Extrusion 85857 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
PolyOne Geon™ Vinyl Rigid Extrusion L0148 Polyvinyl Chloride, Rigid (PVC, Rigid) Note: Finished part testing is required for ASTM E-84 certification. Note: The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by Po.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
LG Chemical LUCEL FW-715C Friction and Wear Resistant POM, Polymeric Wear Additive, CaCo3 Filled, Low Warpage, Antistatic LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Flexural Strength | 77.9 MPa | 11300 psi | ASTM D790 |
Kostat ICP-STAT ICS-1003 PS Sheet KOSTATs ICP-STAT is a thermoplastic sheet coated with an inherently conductive polymer (ICP). ICP-STAT has distinctive advantages in ESD and cleanliness performances compared to other materials bas.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | 2mm/min; ASTM D790 |
Kingfa PA66-T15 15% Mineral Filled PA66 Features:Good size stabilityLow tendency to wrapGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower toolsSport applianceInformation Provided by Kingfa Sci. & .. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | 5 mm/min; ISO 178 |
Gromax BTE30-DN00N1 Nylon 6 (Dry) Information provided by Gromax Enterprises Corp. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP RP004S PA 66 LNP* LUBRICOMP* RP004S is a compound based on Nylon 66 containing PTFE/Silicone. Added features of this grade include: Heat Stabilized, Wear Resistant. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP WL004 PBT LNP LUBRICOMP* WL004 is a compound based on PBT resin containing 20% PTFE. Added features of this material include: Wear Resistant. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX HX8300HP PC+POLYESTER (Asia Pacific) Medium flow, Transparent PC/Polyester alloy. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant... |
|||
Flexural Strength | 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X8300 PC+POLYESTER (Asia Pacific) PC+Polyester, UV Stabilized, Transparent |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP 67001XXH PBT+PC LNP* THERMOCOMP* 67001XXH is a compound based on PC + PBT resin containing proprietary antimicrobial additives. Designed for touch surfaces in patient critical healthcare applications. Added featu.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X8300 PC+POLYESTER (Europe-Africa-Middle East) PC+Polyester, UV Stabilized, Transparent |
|||
Flexural Strength | 77.9 MPa | 11300 psi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP MX92284 PP LNP* THERMOCOMP* MX92284 is a compound based on Polypropylene resin containing Proprietary Filler(s). |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
Styron PULSEâ„¢ 2100 LG PC/ABS Engineering Resin Overview: PULSE 2100LG Engineering Resin is designed to provide top performance in tough applications, from single piece items to intricate components. Ideal for energy management solutions, it can .. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
SABIC Innovative Plastics NORYL N1052P PPE+HIPS (Asia Pacific) PPE+PS 105deg.C FR V-2 |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
SABIC Innovative Plastics NORYL PX0844 PPE+PS PPE+PS blend. Unfilled. UL94 HB rated. Low water absorption. Hydrolytic stability. Dimensional stability. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
Plenco 2369 Phenolic, Granular, Compression Molded PLENCO 02369 is a general purpose, organic filled phenolic molding compound, formulated to minimize the generation of free ammonia for applications that are sensitive to such formation. PLENCO 02369.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
Unitika AXF-1500-05 Conditioned Characteristics: Lubricant grade of AX1500, excellent in heat and chemical resistancesInformation provided by Unitika Ltd. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
Eastman Eastar EN059 Copolyester, Natural Applications:Cosmetics/personal care packagingDeodorant PackagingFragrance packagingOral hygienePlastics for hygiene feminine productsToothbrushesToys/Sporting goodsWriting instrumentsProduct Descri.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® M105 MPPO Resin Flame retardant, Thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Strength | 77.9 MPa | 11300 psi | ASTM D-790 |
Axiall 3152 Rigid PVC, Extrusion Georgia Gulf 3152 is a twin screw powder blend NSF approved for the extrusion of potable water and drain waste and vent pipe application.Information provided by Georgia GulfGeorgia Gulf became Axial.. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | GB/9341 |
Zhejiang Juner PC/PET Alloy Applications: Shell of Small Household Electric Appliance, Auto Electric Appliance PartsInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | 23°C, 50% RH; ASTM D790 |
Asahi Kasei Xyron® A0501 PPE/PA AutomotiveInformation provided by Asahi Kasei |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DBL349E PC (Asia Pacific) LNP* Lubricomp* DBL349E is a compound based on Polycarbonate resin containing Glass Bead, PTFE, Flame Retardant. Added features of this material include:LNP* Lubricomp* DBL349E is a compound based .. |
|||
Flexural Strength | 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X8300CL PC+POLYESTER (Europe-Africa-Middle East) PC+Polyester, UV Stabilized, Transparent, OQ Quality |
|||
Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
SABIC Innovative Plastics NORYL EX130 PPE+HIPS (Asia Pacific) PPE+PS Auto Exterior Grade |