Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
PolyOne Maxxam™ PPH-10G Nat Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Polymer Resources ABS-FR1 ABS, Flame Retardant Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
PolyOne Edgetek® SY-15GB/000 Polystyrene (PS), Glass Bead Filled
(discontinued **) Description/Features:Glass Bead FilledUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Kolon DIAMAT® IH Description: DIAMAT® is a specially formulated high impact grade PMMA resin from KOLON. The acrylic composition results in an excellent balance of impact resistance and high modulus at reasonabl.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790-95 |
Multibase Multi-ABS 3259 Plating Grade Data provided by Multibase. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Techmer ES Elastoblend® PA6 IM 811 HS L (Dry) Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedTPCI# 6109102Information provided by TP Comp.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Techmer ES Elastoblend® PA6 IM 835 HS L Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedProcessing Method: Injection MoldingInformat.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | |
SGL Carbon Group EK 2230 Carbon Graphite Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | |
SGL Carbon Group EK 2243 Carbon Graphite Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | |
SGL Carbon Group V 1626 Graphite Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Techmer ES Plastiblend® ABS 8006 Availability: North AmericaForms: PelletsProcessing Method: Sheet ExtrusionInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SD-0150GP High Impact Grade ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Chase Plastics CP Pryme® A100HI ABS Molding Resin, High Impact Information provided by Chase Plastics. |
|||
Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
Asahi Kasei Thermofil P-40TC-0158 40% Talc Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
Flexural Strength | 58.6 MPa | 8500 psi | 2.0 in/min; ASTM D790 |
LTL Color Compounds ColorFast® GPA300 ABS Super-tough ABS with our highest impact strength, injection moldingAll information provided by LTL Color Compounders, Inc. |
|||
Flexural Strength | 58.6 - 86.2 MPa | 8500 - 12500 psi | |
Bulk Molding Compounds BMC T60-6009 Compression Grade Wear Resistant Molding Compound BMC T60-6009 is a compression grade wear resistant molding compound. This material was specifically formulated for applications that require excellent abrasion resistance. Due to its low specific .. |