- Asahi Kasei Thermofil P-40TC-0158 40% Talc Reinforced, Heat Stabilized
Asahi Kasei Thermofil P-40TC-0158 40% Talc Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermofil |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermofil P-40TC-0158 40% Talc Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Melt Flow | 13 g/10 min | 13 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Flexural Strength | 58.6 MPa | 8500 psi | ASTM D790 |
| Flexural Modulus | 3.59 GPa | 520 ksi | ASTM D790 |
| Izod Impact, Notched | 0.240 J/cm | 0.450 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.74 J/cm | 7.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | ASTM D648 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GTP09005 PVC
- Hexion Bakelite™ PF 1141 Phenolic Formaldehyde Resin, High Surface Quality, Resistant to High Temperatures, Dishwasher Proof
- Solvay Chemicals Strontium carbonate coarse powder
- Polyram RamTal PM3007G2 Polyacetal for Injection Molding, 10% Glass Fiber Reinforced
- Polyram RamTal PM3009G4 Polyacetal for Injection Molding, 20% Glass Fiber Reinforced
- A. Schulman SCHULAMID® 66 GF33H 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- Aremco Ceramabond™ 552 High Temperature Ceramic Adhesive/Paste, Alumina Filled
- Daikin DAI-EL G-912 Fluoroelastomer Terpolymer, Peroxide Curable Grade, 71% Fluorine Content
Copyright © lookpolymers.com All Rights Reserved