Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
Premix Premi-Glas® 2200-25 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2200-25 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal .. |
|||
Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
Premix Premi-Glas® 2203-25 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2203-25 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal .. |
|||
Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
Premix Premi-Glas® 2205-25 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2205-25 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal .. |
|||
Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
Premix Premi-Glas® 3200-25 Fiberglass Reinforced SMC Description: Premi-Glas® 3200-25 is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal and di.. |
|||
Flexural Strength | 155 MPa | 22500 psi | |
Quadrant EPP Duratron® PAI T4301 PAI + graphite + PTFE, extruded (ISO Data) The addition of PTFE and graphite provides higher wear resistance and lower coefficient of friction compared to the unfilled grade as well as a lower tendency to stick-slip. Duratron T4301 PAI also .. |
|||
Flexural Strength | 155 MPa | 22500 psi | ISO 178 |
SABIC Innovative Plastics LNP FARADEX ES003E PEI LNP* FARADEX* ES003E is a Polyetherimide resin containing 15% Stainless Steel Fibers. Added feature of this grade is: EMI/RFI Shielding. |
|||
Flexural Strength | 155 MPa | 22500 psi | STN EN ISO 178 |
Plastcom SLOVAMID 6 GF 15 FRA 5 Polyamide 6, 15% Glass Fiber, Halogen Flame Retardant FeaturesPA 6 for injection moulding, chemically reinforced with 15% glass fiber, with halogen flame retardant. Main features: flammability in accordance with UL 94 V0 at 1.6mm, glow wire at 960°C,.. |
|||
Flexural Strength | 155 MPa @Thickness 3.17 mm |
22500 psi @Thickness 0.125 in |
ASTM D790 |
PTS Tristar® PC-30GFR 30% Glass Reinforced Polycarbonate Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
PolyOne Edgetek® PF-20CF/000 Polysulfone
(discontinued **) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for .. |
|||
Flexural Strength | 155 MPa | 22500 psi | |
Lehmann & Voss LUVOCOM® 19-8373 Polyamide 46, with carbon fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Antistatic.Improved fri.. |
|||
Flexural Strength | 155 MPa | 22500 psi | 1.3 mm/min; ASTM D790 |
Lavergne VYPET VNT 615 FR PET 15% Glass Reinforced, Flame Retardant Vypet VNT 615 FR is a 15% fiberglass reinforced flame retardant PET injection molding compound designed for electrical and structural applications.Features: Flame retardant; UL yellow card file E216.. |
|||
Flexural Strength | 155 MPa | 22500 psi | |
Haysite HCR-125 Corrosion Resistant Vinyl Ester/Glass Sheet A fiber glass reinforced thermoset sheet using DEREKANE® 470 vinylester in the resin matrix with flame retardant and ultraviolet inhibitors. Standard color is beige. Derakane® 470 is a registe.. |
|||
Flexural Strength | 155 MPa | 22500 psi | 5 mm/min; ISO 178 |
Gromax BFG10-BN00N1 Nylon 6 10% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
Techmer ES Electrafil® M-2426 BK Polycarbonate |
|||
Flexural Strength | 155 MPa | 22500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 4521 PBT (Europe-Africa-Middle East) VALOX 4521 is a high flow, 19.5% glass reinforced flame retardant PBT injection moulding resin. Applications: electrical applications. |
|||
Flexural Strength | 155 MPa | 22500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 815 PBT (Europe-Africa-Middle East) VALOX 815 is a 15% glass reinforced PBT+PET blend with excellent surface finish. Applications: hot air gun housings assemblies, industrial glue guns, appliance housings and handles. |
|||
Flexural Strength | 155 MPa | 22500 psi | 2mm/min; ISO 178 |
Teijin Panlite® G-3430H Low Anisotropy, Glass Fiber Reinforced Polycarbonate Resin Reinforced with 30 % of special GF and improved appearance grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need good appearance and mechanical propertyPreci.. |
|||
Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
Unitika M1030E PA6, Dry Nano composite nylonInformation provided by Unitika Ltd. |
|||
Flexural Strength | 155 MPa | 22500 psi | ISO 178-93 |
Wellman EcoLon® MRGF1914-BK1 Nylon 66, 40% Mineral and Glass Reinforced All information provided by Wellman Engineered Resins. |
|||
Flexural Strength | 155 MPa | 22500 psi | ISO 178-93 |
Wellman Wellamid® GFT1628-BK 17% Glass Fiber Reinforced, Impact Modified Nylon 66 Description: Glass Fiber Reinforced, Impact Modified Nylon 66Information provided by Wellman. |
|||
Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
A. Schulman SCHULAMID® 66 GF13 13% Glass Fiber Reinforced Nylon 66 Information provided by A. Schulman. |
|||
Flexural Strength | 155 MPa | 22500 psi | cond; ISO 178 |
DSM Novamid® 1010GN2-20 NAT/BK37 PA6-GF20 FR(17) 20% Glass Reinforced, Flame Retardant |
|||
Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® 304-G20 PBT Resin 20% glass fiber reinforced, flame retardant, low bleeding, UV-resistantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Strength | 155 MPa | 22500 psi | dry; ISO 178 |
DSM Novamid® 1013PL1 NAT PA6-MX Injection Molding |
|||
Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® MN201-G20 Nylon 66 Resin 20% glass fiber reinforced, thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group) |