Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 1.40 GPa | 203 ksi | 4 mm thick;10.0 mm wide molded rod; ISO 178 |
Premix Thermoplastics PRE-ELEC® PP 1386 PRE-ELEC PP 1386 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE.. |
|||
Modulus of Elasticity | 1.40 GPa | 203 ksi | ISO 178 |
Premix Thermoplastics PRE-ELEC® PP 1395 PRE-ELEC PP 1395 is a dissipative thermoplastic compound based on polypropylene. The electrical dissipation is achieved by using special conductive carbon black. In addition to stable surface resist.. |
|||
Modulus of Elasticity | 1.40 - 2.00 GPa | 203 - 290 ksi | ASTM D638-04 |
Proto3000 Objet Digital Materials™ DM_8425 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide.. |
|||
Modulus of Elasticity | 1.40 - 2.00 GPa | 203 - 290 ksi | ASTM D638-04 |
Proto3000 Objet Digital Materials™ DM_8505Gray50 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr.. |
|||
Modulus of Elasticity | 1.40 GPa | 203 ksi | DIN 53457 |
Ineos Nova S-6600MG Compact Polystyrene Microgranulates
(discontinued **) High impact polystyrene Microgranulates, having a diameter of 0.8 - 1.0 mm especially useful for compounding and extrusion applications. Due to the higher viscosity intensive mixing with thermoplas.. |
|||
Modulus of Elasticity | 1.40 - 2.80 GPa | 203 - 406 ksi | Average value: 2.10 GPa Grade Count:61 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded". Each property range of values reported is .. |
|||
Modulus of Elasticity | 1.40 - 5.12 GPa | 203 - 743 ksi | Average value: 2.33 GPa Grade Count:141 |
Overview of materials for Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced". Each property range of values repor.. |
|||
Modulus of Elasticity | 1.40 - 3.30 GPa | 203 - 479 ksi | Average value: 2.46 GPa Grade Count:26 |
Overview of materials for Polypropylene with 40% Calcium Carbonate (CaCO3) Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Calcium Carbonate (CaCO3) Filler". Specific grades with primary filler content be.. |
|||
Modulus of Elasticity | 1.40 - 10.0 GPa | 203 - 1450 ksi | Average value: 3.12 GPa Grade Count:6 |
Overview of materials for Nylon, Amorphous Transparent Alloy This property data is a summary of similar materials in the MatWeb database for the category "Nylon, Amorphous Transparent Alloy". Each property range of values reported is minimum and maximum value.. |
|||
Modulus of Elasticity | 1.40 GPa @Temperature -40.0 °C |
203 ksi @Temperature -40.0 °F |
ASTM D638 |
Micropol Isoplas P501 Crosslinkable Polyethylene Information provided by Micropol Limited |
|||
Modulus of Elasticity | 1.40 GPa | 203 ksi | ISO 527-2 |
Tisan TISOPLEN® 10% Calcite Filled Heat Stabilized Homopolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Modulus of Elasticity | 1.40 - 1.40 GPa @Temperature 120 - 120 °C |
203 - 203 ksi @Temperature 248 - 248 °F |
Average value: 1.40 GPa Grade Count:1 |
Overview of materials for Cellulose Acetate Propionate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate Propionate, Molded". Each property range of values reported is minimum and maximum val.. |
|||
Modulus of Elasticity | 1.40 - 5.17 GPa | 203 - 750 ksi | Average value: 3.21 GPa Grade Count:45 |
Overview of materials for Polypropylene with 40% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 40% Talc Filler". Specific grades with primary filler content between 35% and 44% are.. |