Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 5.52 - 12.4 GPa | 800 - 1800 ksi | Average value: 9.72 GPa Grade Count:16 |
Overview of materials for Polyetherimide (PEI), 30% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 30% Glass Fiber". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Modulus of Elasticity | 5.52 GPa | 800 ksi | ASTM D638 |
ITW Devcon Metal Repair Aluminum Putty (F), Aluminum Information provided by ITW Devcon |
|||
Modulus of Elasticity | 5.52 GPa | 800 ksi | ASTM D638 |
ITW Devcon Metal Repair Bronze Putty (BR), Bronze Information provided by ITW Devcon |
|||
Modulus of Elasticity | 5.52 GPa | 800 ksi | ASTM D638 |
ITW Devcon Metal Repair Stainless Steel Putty (ST), Grey Information provided by ITW Devcon |
|||
Modulus of Elasticity | 5.52 GPa | 800 ksi | In Tension; ASTM D638 |
Devcon Carbide Putty Epoxy Abrasion-Resistant SystemComments: PuttyData provided by Ellsworth Adhesives. |
|||
Modulus of Elasticity | 5.52 GPa | 800 ksi | In Tension; ASTM D638 |
Devcon Combo Wear FC Epoxy Abrasion-Resistant SystemComments: PuttyData provided by Ellsworth Adhesives. |
|||
Modulus of Elasticity | 5.52 GPa | 800 ksi | In Tension; ASTM D638 |
Devcon Tile Adhesive Epoxy Abrasion-Resistant SystemComments: PuttyData provided by Ellsworth Adhesives. |
|||
Modulus of Elasticity | 5.52 GPa | 800 ksi | |
3M Scotch-Weld™ 2214 Hi-Temp Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids, 3M™ Sc.. |
|||
Modulus of Elasticity | 5.52 - 14.5 GPa | 800 - 2100 ksi | Average value: 10.9 GPa Grade Count:10 |
Overview of materials for Polyetherimide (PEI), Nickel Coated Graphite Filled This property data is a summary of similar materials in the MatWeb database for the category "PEI, NCG Filled". Each property range of values reported is minimum and maximum values of appropriate Ma.. |
|||
Modulus of Elasticity | 5.52 - 9.17 GPa | 800 - 1330 ksi | Average value: 6.83 GPa Grade Count:7 |
Overview of materials for Polyphthalamide (PPA), 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are .. |
|||
Modulus of Elasticity | 5.52 - 19.3 GPa | 800 - 2800 ksi | Average value: 11.7 GPa Grade Count:24 |
Overview of materials for Polyphthalamide (PPA), Glass/PTFE This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide + Glass/PTFE". Each property range of values reported is minimum and maximum values of a.. |