Devcon Carbide Putty Epoxy
| Category | Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive |
| Manufacturer | Devcon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Devcon Carbide Putty Epoxy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Abrasion-Resistant SystemComments: PuttyData provided by Ellsworth Adhesives.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 85 | 85 | ASTM D2240 |
| Tensile Strength, Ultimate | 18.2 MPa | 2640 psi | ASTM D638 |
| Modulus of Elasticity | 5.52 GPa | 800 ksi | In Tension; ASTM D638 |
| Flexural Yield Strength | 37.8 MPa | 5480 psi | ASTM D790 |
| Compressive Yield Strength | 56.3 MPa | 8160 psi | ASTM D695 |
| Adhesive Bond Strength | 9.31 MPa | 1350 psi | Adhesive tensile shear strength; ASTM D1002 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 µm/m-°C @Temperature 20.0 °C |
13.9 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | 0.523 W/m-K | 3.62 BTU-in/hr-ft²-°F | ASTM C177 |
| Maximum Service Temperature, Air | 121 °C | 250 °F | Operating Temperature |
| Shrinkage | 0.090 % | 0.090 % | During Cure; ASTM D2566 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 25 | 25 | ASTM D150 |
| Dielectric Strength | 7.87 kV/mm | 200 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 21.1 °C | 70.0 °F | |
| Pot Life | 50.0 min @Temperature 23.9 °C |
50.0 min @Temperature 75.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Coverage per lb. | 64 in² | at 1/4 inch thick |
| Mix Ratio by Volume | 4 to 1 | resin:hardener |
| Mix Ratio By Weight | 8 to 1 | resin:hardener |
Users viewing this material also viewed the following:
- MV Labs RU400 RuCl3·xH2O Ruthenium(III) chloride hydrate
- Quadrant EPP TIVAR® Polysteel Filled UHMW-PE, High Specific Gravity (ASTM Product Data Sheet)
- SABIC Innovative Plastics Lexan® ML6411 PC Copolymer
- Abatron AboCast 8-11/Abocure 8-11 Epoxy (discontinued **)
- Kotec Carbotex KG-10MRA Polycarbonate, 10% Glass Fiber Reinforced
- SABIC Innovative Plastics Valox® 8032UX PBT+PET
- A. Schulman POLYBATCH™ U-4444-E Blowing Agent Concentrate Based In PE
- Clariant Renol PA211G40 Nylon 6, 40% Glass Fiber, Lubricated
- 3M Scotchkote™ 165CS Urethane Sealer
- Eastman Tenite Butyrate 581A3720016 Clear, Trsp Cellulose Acetate Butyrate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved