Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 165 MPa @Temperature 23.9 °C |
24000 psi @Temperature 75.0 °F |
Dry; 325°F, 1000psi Cured; ASTM D695 |
Park Electrochemical Nelcote® F-502 Phenolic Prepreg, Silica Reinforced Nelcote® F-502 is a MIL-R-9299 phenolic resin system suitable for impregnation on any MIL-C-9084 fabric with a compatible finish. F-502 is used in the manufacture of ablative reinforcements in rock.. |
|||
Compressive Strength | 165 MPa @Temperature 23.9 °C |
24000 psi @Temperature 75.0 °F |
Dry; 325°F Autoclave; ASTM D695 |
Park Electrochemical Nelcote® F-554 Phenolic Prepreg, Aerospace Silica Fabric Reinforced Nelcote® F-554 is a high purity silica filled phenolic resin coated on Commercial or Aerospace grade silica fabric. F-554 is used in the manufacture of intermediate temperature ablative rocket nozz.. |
|||
Compressive Strength | 165 MPa @Temperature 23.9 °C |
24000 psi @Temperature 75.0 °F |
Dry; 325°F Autoclave; ASTM D695 |
Park Electrochemical Nelcote® F-557 Phenolic Prepreg, Commercial Silica Fabric Reinforced Nelcote® F-557 is a high purity silica filler phonic resin coated on Commercial or Aerospace grade silica fabric. F-557 is used in the manufacture of intermediate temperature ablative rocket nozzle.. |
|||
Compressive Strength | 165 MPa @Temperature 23.9 °C |
24000 psi @Temperature 75.0 °F |
Dry; ASTM D695 |
Park Electrochemical Nelcote® S-860 Silicone Prepreg, 1581-112NPH E-Glass Reinforced Nelcote® S-860 is a MIL-P-25518 type silicone resin with a good combination of electrical and high temperature properties. GMS4001 qualified specificationsKey Features and Benefits:500°F maximum s.. |
|||
Compressive Strength | 165 MPa | 24000 psi | 10% Def.; ASTM D695 |
Quadrant EPP Duratron® PAI T4203 Extruded Polyamide-imide (ASTM Product Data Sheet) |
|||
Compressive Strength | 165 MPa | 24000 psi | 10% Def.; ASTM D695 |
Quadrant EPP Semitron® MPR-1000 (ASTM Product Data Sheet) |
|||
Compressive Strength | 165 MPa | 24000 psi | 10% Def.; ASTM D695 |
Quadrant EPP Techtron® PSGF PPS - Compression Molded 40% Glass Reinforced Polyphenylene Sulfide (ASTM Product Data Sheet) |
|||
Compressive Strength | 165 MPa | 24000 psi | 10% Def.; ASTM D695 |
Quadrant EPP Semitron® CMP XL20 (ASTM Product Data Sheet) |
|||
Compressive Strength | 165 MPa | 24000 psi | ASTM D695 |
Techmer ES Plaslube® J-1/30/TF/13/SI/2 NAT PA66 |
|||
Compressive Strength | >= 165 MPa | >= 24000 psi | |
Master Bond EP46HT-2Med Two Component Heat Resistant Biocompatible Epoxy System Master Bond Polymer System EP46HT-2MED is a two component medical grade epoxy system for high performance structural bonding and casting suitable for applications where resistance to temperatures fr.. |
|||
Compressive Strength | 165 MPa | 24000 psi | Lengthwise; ASTM D635 |
Bedford Plastics Glass Reinforced FR Polyester Flat Sheet, 1/8" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod.. |
|||
Compressive Strength | 165 MPa | 24000 psi | Lengthwise; ASTM D635 |
Bedford Plastics Glass Reinforced FR Polyester Flat Sheet, 3/16" to 1/4" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod.. |
|||
Compressive Strength | 165 MPa | 24000 psi | Lengthwise; ASTM D635 |
Bedford Plastics Glass Reinforced Polyester Flat Sheet, 3/16" to 1/4" Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded products feature:High StrengthCorrosion Resistant to many che.. |
|||
Compressive Strength | 165 MPa | 24000 psi | Lengthwise; ASTM D635 |
Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 1/8" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod.. |
|||
Compressive Strength | 165 MPa | 24000 psi | Lengthwise; ASTM D635 |
Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 3/16" to 1/4" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod.. |
|||
Compressive Strength | 165 MPa | 24000 psi | ASTM D695 |
Applied Composites 8038 Polyester SMC Industry Application: TransportationProduct Application: Mass TransitDistinct Features: Low Smoke Construction and Mass Transit, Oxygen Matex 80+, E84-61 TunnelInformation provided by Applied Compos.. |
|||
Compressive Strength | 165 - 193 MPa | 24000 - 28000 psi | |
Bulk Molding Compounds BMC 5209 Mineral Filled, Glass Reinforced Polyester BMC 5209 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is a high impact material produced in ex.. |
|||
Compressive Strength | 165 - 193 MPa | 24000 - 28000 psi | |
Bulk Molding Compounds BMC 605L Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 605L molding compound is a low cost, mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is characterized by good molda.. |
|||
Compressive Strength | 165 MPa | 24000 psi | Lengthwise; ASTM D635 |
Bedford Plastics Glass Reinforced Polyester Flat Sheet 1/8" Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded products feature:High StrengthCorrosion Resistant to many che.. |
|||
Compressive Strength | 165 MPa | 24000 psi | Lengthwise; ASTM D635 |
Bedford Plastics Glass Reinforced Polyester Flat Sheet, 3/8" to 1" Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded products feature:High StrengthCorrosion Resistant to many che.. |
|||
Compressive Strength | 165 - 193 MPa | 24000 - 28000 psi | |
Bulk Molding Compounds BMC 5209-12940 Mineral Filled, Glass Reinforced Polyester BMC 5209-12940 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is a high impact material produced.. |
|||
Compressive Strength | 165 - 193 MPa | 24000 - 28000 psi | |
Bulk Molding Compounds BMC 5338 Mineral Filled, Glass Reinforced Polyester BMC 5338 molding compound is a mineral Filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is a high impact material produced in ex.. |
|||
Compressive Strength | 165 - 193 MPa | 24000 - 28000 psi | |
Bulk Molding Compounds BMC 605 Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 605 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is characterized by good moldability, medi.. |
|||
Compressive Strength | 165 - 193 MPa | 24000 - 28000 psi | |
Bulk Molding Compounds BMC 610 Mineral Filled, Glass Reinforced Polyester Compound BMC 610 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is set a part form other medium impact el.. |
|||
Compressive Strength | 165 - 193 MPa | 24000 - 28000 psi | |
Bulk Molding Compounds BMC 620M Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 620M molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, and stuffer injection molding It is characterized by high impact strength, good mol.. |
|||
Compressive Strength | 165 MPa | 24000 psi | ASTM D695 |
PolyOne Edgetek® NL-30CF/000 Nylon 6/12, Carbon Fiber Reinforced
(discontinued **) Description/Features:Carbon Fiber ReinforcedInformation provided by PolyOne Corporation. |
|||
Compressive Strength | 165.5 MPa | 24000 psi | |
Henkel Hysol EA 9394/C-2 Paste Adhesive System Elevated cure, thixotropic adhesive with structural properties to 450°F / 232°C.Application: Structural Repair |