Bulk Molding Compounds BMC 605 Mineral Filled, Glass Fiber Reinforced Polyester Compound

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS , Thermoset Polyester Glass and Mineral Filled BMC
Manufacturer	BMC - Bulk Molding Compounds Inc.
Trade Name	BMC
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Bulk Molding Compounds BMC 605 Mineral Filled, Glass Fiber Reinforced Polyester Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BMC 605 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is characterized by good moldability, medium impact strength, excellent overall electrical properties and flame resistance.Typical applications include circuit breakers, transformer bobbins and motor end bells.

Physical Properties	Metric	English	Comments
Specific Gravity	1.95 g/cc	1.95 g/cc
Water Absorption	0.14 %	0.14 %	24 hours, 23°C
Linear Mold Shrinkage	0.0025 - 0.0040 cm/cm	0.0025 - 0.0040 in/in

Mechanical Properties	Metric	English
Hardness, Barcol	40 - 50	40 - 50
Tensile Strength, Ultimate	41.4 - 55.2 MPa	6000 - 8000 psi
Flexural Strength	110 - 138 MPa	16000 - 20000 psi
Compressive Strength	165 - 193 MPa	24000 - 28000 psi
Izod Impact, Notched	1.07 - 3.20 J/cm	2.00 - 6.00 ft-lb/in

Thermal Properties	Metric	English
Deflection Temperature at 1.8 MPa (264 psi)	>= 260 °C	>= 500 °F
Flammability, UL94	V-0 @Thickness 6.35 mm	V-0 @Thickness 0.250 in
	V-0 @Thickness 3.17 mm	V-0 @Thickness 0.125 in
	V-0 @Thickness 1.59 mm	V-0 @Thickness 0.0625 in

Electrical Properties	Metric	English	Comments
Dielectric Strength	13.8 kV/mm	350 kV/in	Short Time
Arc Resistance	190 sec	190 sec
Comparative Tracking Index	>= 600 V	>= 600 V

Processing Properties	Metric	English	Comments
Mold Temperature	138 - 166 °C	280 - 330 °F