Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 35.0 MPa | 5080 psi | ASTM D638 |
Premix Premi-Glas® 1200-15 Fiberglass Reinforced Thermoset SMC Premi-Glas® 1200-15 is a fiberglass reinforced thermoset sheet molding compound for general purpose applications requiring thermal stability and stiffness.Key features and benefits are:Excellent st.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ASTM D638 |
Premix Premi-Glas® 1201-15 Polyester SMC Premi-Glas® 1201-15 is a 15% glass reinforced thermoset Sheet Molding Compound designed for sinks, shower stall bases and wall applications. Key features and benefits are:Supports ANSI 124.2 and CS.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ASTM D638 |
Premix Premi-Glas® 1240-15 Fiberglass Reinforced Thermoset Thick Molding Compound Premi-Glas® 1240-15 is a fiberglass reinforced thermoset Thick Molding Compound for general purpose applications requiring thermal stability and stiffness.Key features and benefits are:Excellent st.. |
|||
Tensile Strength | 35.0 - 140 MPa | 5080 - 20300 psi | MD; ISO 527 / PA_098 |
Quadrant Plastic Composites GMT Glass-Mat-Reinforced Thermoplastic This semi-finished product in panel form was developed primarily as a substitute for metals (steel, aluminum etc.) and its main purchasers can be found in the automotive industry. This is where it i.. |
|||
Tensile Strength | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group RALUPOL® 4802 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u.. |
|||
Tensile Strength | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group RALUPOL® 5000 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, very good electrical values, excellent heat resistance, good mechanical strength. This product meets the all.. |
|||
Tensile Strength | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group RALUPOL® 802 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength, good heat resistance. This product meets the allowed up.. |
|||
Tensile Strength | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group RALUPOL® 804 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy m.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ASTM D412 |
GRECO ISOTHANE 1190A Poly(adipate)ester TPUÂ Resin ISOTHANE 1100 series products are transparent grade, polyester poly(adipate)ester based thermoplastic polyurethanes. They exhibit good toughness, solvent resistance, easy processing, and high transp.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | Measured on films cast from solution in toluene; ISO 37 |
Kraton® G1650 E (SEBS) Linear Triblock Copolymer Description: Kraton G1650 E is a clear linear triblock copolymer based on styrene and ethylene/butylene, S-E/B-S, with bound styrene of 29.2% mass. It is supplied from Europe in the physical forms i.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | Weld; ASTM D638 |
Kuraray Genestarâ„¢ GW2458HF Nylon, 45% Glass Filled Low Warpage, High Flow V-0 Grade. It is suited for low warpage and high flow applications, making it well suited for card connectors. |
|||
Tensile Strength | 35.03 MPa | 5080 psi | ISO 527-2/5A/500 |
Lubrizol Advanced Materials Pearlthane® D91T80 Thermoplastic Polyurethane Type : Pearlthane® D91T80 is a aliphatic-based thermoplastic polyurethane.Main Application : Injection MouldingSpecial Features : Low density, fast processing and excellent elasticity properties... |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ISO 527-1 |
Sax Polymers SAXLAC 340Q Acrylonitrile Butadiene Styrene Saxalac 340Q is an siliconized, UV protected, high impact resistant and easy flowing ABS injection molding grade, characterized by good processability and high stiffness.Mechanical property data tes.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ASTM D412 |
Wanhua Chemical Wanthane® WHT-7185 Polycaprolactone Based TPU Higher mechanical strength, good hydrolytic stability & chemical resistance, weather resistance, heat & fungus resistanceInformation provided by Wanhua Chemical Group Co., Ltd. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ASTM D412 |
Wanhua Chemical Wanthane® WHT-1495B Polyester Based TPU Good extrusion stability, high transparency, excellent mechanical propertiesInformation provided by Wanhua Chemical Group Co., Ltd. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | |
Corbion Purac Blend C High Heat, Impact Modified Homopolymer PLA Heat resistance higher than typical PLA is achieved by addition of a nucleating agent and PDLA homopolymer. Increased impact is produced by addition of impact modifier to the base grade; a small am.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | DIN 53 455 |
Hippe PA 12 Nylon 12 Maintenance-free bearing and gear components under water, insulated components, seals, gear wheels. Parts for pumps and household units. Application in the electrical sector - less water absorptio.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | DIN 53 455 |
Hippe PP Polypropylene Lower density compared with PE. Higher hardness and stiffness and better reset features. Non-fragile. Toughness in cold lesser than that of PE. Higher working temperatures than PE, not aromatic-.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ISO 37 |
BASF Elastollan 1085 A TPUR Description: Thermoplastic Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, high tear and tensile strength, good damping characteristics and a high resilien.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | after storage in water at 80°C for 42 days; ISO 37 |
BASF Elastollan C 75 A HPM TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping c.. |
|||
Tensile Strength | 35.0 MPa @Strain 2.00 %, Temperature 40.0 °C |
5080 psi @Strain 2.00 %, Temperature 104 °F |
50 mm/min; ISO 527-2 |
BASF Elastollan R 3000 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan.. |
|||
Tensile Strength | >= 35.0 MPa | >= 5080 psi | ISO 37 |
Austin Novel Materials Texalan® 282A Polyester-based TPU Description: Good abrasion resistance, tensile strength, oil resistance and transparency which can meet different demands in various industryInformation from Dawnentech |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ISO 37 |
BASF Elastollan 670 AWHU TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and wear resistance, good damping characteristics and a high resilience performance.Typical Applicat.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | after storage in water at 80°C for 42 days; ISO 37 |
BASF Elastollan C 75 A TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping c.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | after storage in water at 80°C for 42 days; ISO 37 |
BASF Elastollan C 85 A HPM TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping c.. |
|||
Tensile Strength | 35.0 MPa @Strain 5.00 %, Temperature 60.0 °C |
5080 psi @Strain 5.00 %, Temperature 140 °F |
50 mm/min; ISO 527-2 |
BASF Elastollan R 2000 20% Glass Filled TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with exceptional properties, very high impact resistance, high modulus with at the same time elasticity, low coefficient of thermal expan.. |
|||
Tensile Strength | 35.0 - 60.0 MPa | 5080 - 8700 psi | Compression; ISO 527 |
Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl phthalate molding compound free from halogens. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exc.. |
|||
Tensile Strength | 35.0 MPa | 5080 psi | wrap; ISO 37 Type 2 |
Rogers Corporation Bisco® A2 R 1.0 Engineered Solid Silicone Mass Layer, Fiberglass Reinforced Sound Barrier BISCO® A2 Fiberglass Reinforced Sound Barrier provides a similar level of sound absorption and flame resistance as the non-reinforced A2 Sound Barrier with the addition of increased tensile and tea.. |
|||
Tensile Strength | >= 35.0 MPa | >= 5080 psi | ISO 37 |
Austin Novel Materials Texalan® 385A Polyester-based TPU Description: Good abrasion resistance, tensile strength, oil resistance which can be used in injection, extrusion purpose.Information from Dawnentech |
|||
Tensile Strength | 35.0 MPa | 5080 psi | ISO 37 |
BASF Elastollan B 60 A WHA TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, high tensile strength, good damping and resilience performance and sup.. |