BASF Elastollan 1185 A WM TPUR

Category	Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyether Grade
Manufacturer	BASF
Trade Name	Elastollan
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	BASF Elastollan 1185 A WM TPUR.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Description: Thermoplastic Polyether Polyurethane Elastomers with outstanding hydrolysis resistance, low temperature flexibility and resistance to micro-organisms.Typical Applications: Cable sheathing, plugs and terminations, spiral tubing, films, ski boot shells, ear tags, technical moldings, e.g. mining screens, railway pads and seals.Note: Quoted results are from measurements on injection molded test platens, post tempered for 20 hours at 100°CInformation provided by BASF

Physical Properties	Metric	English	Comments
Density	1.15 g/cc	0.0415 lb/in³	ISO 1183-1-A

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	87	87	ISO 868
Hardness, Shore D	39	39	ISO 686
Tensile Strength	30.0 MPa	4350 psi	after storage in water at 80°C for 42 days; ISO 37
	35.0 MPa	5080 psi	ISO 37
	4.00 MPa <br>@Strain 20.0 %	580 psi <br>@Strain 20.0 %	ISO 37
	7.00 MPa <br>@Strain 100 %	1020 psi <br>@Strain 100 %	ISO 37
	13.0 MPa <br>@Strain 300 %	1890 psi <br>@Strain 300 %	ISO 37
Elongation at Break	600 %	600 %	ISO 37
	600 %	600 %	after storage in water at 80°C for 42 days; ISO 37
Charpy Impact, Notched	NB <br>@Temperature -30.0 °C	NB <br>@Temperature -22.0 °F	DIN EN ISO 179
	NB <br>@Temperature 23.0 °C	NB <br>@Temperature 73.4 °F	DIN EN ISO 179
Tear Strength	55.0 kN/m	314 pli	DIN ISO 34-1/Bb
Abrasion	38	38	[mm<sup>3</sup>; ISO 4649
Compression Set	20 % <br>@Temperature 23.0 °C	20 % <br>@Temperature 73.4 °F	ISO 815
	35 % <br>@Temperature 70.0 °C	35 % <br>@Temperature 158 °F	ISO 815

Processing Properties	Metric	English	Comments
Processing Temperature	160 - 220 °C	320 - 428 °F	Extrusion
Mold Temperature	20.0 - 70.0 °C	68.0 - 158 °F

Descriptive Properties	Value	Comments
Commercial Status	North America
Primary Processing Technique	Extrusion