Corbion Purac Blend C High Heat, Impact Modified Homopolymer PLA

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer
Manufacturer	Corbion Purac
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Corbion Purac Blend C High Heat, Impact Modified Homopolymer PLA.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Heat resistance higher than typical PLA is achieved by addition of a nucleating agent and PDLA homopolymer. Increased impact is produced by addition of impact modifier to the base grade; a small amount of talc is added to preserve the modulus. Data is for samples produced from Puralact L and D lactide monomers. PLA is 100% biobased and is both recyclable and compostable. PLA can be used in a broad range of applications from molded plastic parts to textiles, foams, and films.Information provide by Corbion Purac.

Physical Properties	Metric	English	Comments
Density	1.25 g/cc	0.0452 lb/in³

Mechanical Properties	Metric	English
Tensile Strength	35.0 MPa	5080 psi
Elongation at Break	60 %	60 %
Tensile Modulus	3.50 GPa	508 ksi
Charpy Impact, Notched	2.30 J/cm²	10.9 ft-lb/in²

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	HDT B flatwise

Processing Properties	Metric	English	Comments
Melt Temperature	190 - 220 °C	374 - 428 °F	pre-drying required
Mold Temperature	70.0 - 100 °C	158 - 212 °F

Descriptive Properties	Value	Comments
Clarity	No