Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 5.0 - 7.0 g/10 min | 5.0 - 7.0 g/10 min | (Condition L) ASTM D-1238 |
Multibase Multi-Flex® TPE A 8615 BLK This material is currently used in caster wheels where higher abrasion resistance is required. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Melt Flow | 4.5 - 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.5 - 7.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
NIZHNEKAMSKNEFTEKHIM PP 1500L (C30G) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
Melt Flow | 5.0 - 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 - 7.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
NIZHNEKAMSKNEFTEKHIM PP 4210L (EP2C30F) Propylene and Ethylene Copolymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r.. |
|||
Melt Flow | 5.0 - 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 - 7.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
NIZHNEKAMSKNEFTEKHIM PP 7445L (EPC57MA) Propylene and Ethylene Block Polymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r.. |
|||
Melt Flow | 3.0 - 7.0 g/10 min | 3.0 - 7.0 g/10 min | ASTM D1238 |
Polymer Resources PCSF-FR G30 Polycarbonate, 30% Glass Reinforced Structural Foam Grade Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel.. |
|||
Melt Flow | 2.0 - 7.0 g/10 min @Load 11.6 kg, Temperature 250 °C |
2.0 - 7.0 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
Polymer Resources PPX-GP5 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 270F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
Melt Flow | 3.0 - 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.0 - 7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Ravago Manufacturing Americas Hylex® P1010G30 HB Polycarbonate, 30% Fiberglass Reinforced Information provided by Ravago. |
|||
Melt Flow | 3.0 - 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.0 - 7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Ravago Manufacturing Americas Hylex® P1310G30 HB Polycarbonate, 30% Fiberglass Reinforced, UV Stabilized Information provided by Ravago. |
|||
Melt Flow | 6.0 - 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 - 7.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
FKuR Kunststoff Terralene® HD 3505 Biobased Polyethylene With the brand name Terralene® FKuR offers biobased polyethylene compounds made using Braskem's Green PE. When compared to conventional polyethylene (PE), the main difference is that the ethanol.. |
|||
Melt Flow | 4.1 - 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.1 - 7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Iran Petrochemical (PCC) PC 0407 Polycarbonate Suitable for extrusion, injection, and blow moldingInformation provided by Iran Petrochemical Commercial Co. |
|||
Melt Flow | 4.0 - 7.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
4.0 - 7.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238 |
Gromax CCP PBT 1100-211X Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Melt Flow | 2.0 - 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.0 - 7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
LTL Color Compounds Surlyn Reflection Series® SURSG201UG Surlyn Resin/Nylon 6 Alloy A patented alloy of DuPont™ Surlyn® resin and nylon 6 for applications that require a high gloss, molded in color surface finish directly from the mold.All information provided by LTL Color .. |
|||
Melt Flow | 3.0 - 7.0 g/10 min @Load 2.16 kg, Temperature 150 °C |
3.0 - 7.0 g/10 min @Load 4.76 lb, Temperature 302 °F |
|
Taiwan Sheen Soon Sheenthane® AH-782 TPU for Hotmelt Adhesive Thermoplastic polyurethane elastomer for hotmelt adhesiveNon-yellowing, aliphatic gradeExcellent bonding strength for polyester, TPU, nylon, PVC, leather, fabrics, etc. Melt flow may be customized... |
|||
Melt Flow | 3.0 - 7.0 g/10 min | 3.0 - 7.0 g/10 min | Cond L; ASTM D1238 |
Washington Penn PPH2TF-2B Polypropylene, 20% Talc Filled Injection Molding Grade. Heat Stabilized. Meets Ford ESH-M4D293-B Spec.Applications: AC Blower wheels, parts and appliances.Data provided by Washington Penn Plastic Co., Inc. |
|||
Melt Flow | 4.0 - 7.0 g/10 min | 4.0 - 7.0 g/10 min | Cond L; ASTM D1238 |
Washington Penn PPH5CF75 Polypropylene, 75% Calcium Carbonate Filled Concentrate UV Stabilized.Applications: ShelvingData provided by Washington Penn Plastic Co., Inc. |
|||
Melt Flow | 5.0 - 7.0 g/10 min | 5.0 - 7.0 g/10 min | ISO 1133 |
Chengdu Polyster H4040 Thermoplastic Polyether-ester Elastomer (TPEE) Low modulus molding and injection grade. Contains improved color- stable antioxidants. Excellent flex resistance, especially at low temperatures. Moldable even in thin sections. Can be used in light.. |
|||
Melt Flow | 5.0 - 7.0 g/10 min | 5.0 - 7.0 g/10 min | |
Biomer P240 PHB Biodegradable Polymer PHB is a isotactic, absolutely linear, thermoplastic homopolyester built of 3-hydroxy butyric acid. The formula of the subunit is -[O-CH(CH3)-CH2-CO]-. PHB is free from even traces of catalysts. P.. |
|||
Melt Flow | 3.0 - 7.0 g/10 min | 3.0 - 7.0 g/10 min | |
Asahi Glass Fluon® P-65P PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Melt Flow | 3.0 - 7.0 g/10 min | 3.0 - 7.0 g/10 min | |
Asahi Glass Fluon® P-805UP PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
Melt Flow | 3.0 - 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 - 7.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
AKG Polymers Vision PP PPH Jazz0502dark Polypropylene Homopolymer Compound Vision consists of a complete assortment of high-quality compounds based on industrial PP waste.Applications: Automotive, Non-food packaging, Storage/transport systems, Road and hydraulic Engineerin.. |
|||
Melt Flow | 2.0 - 7.0 g/10 min @Load 5.00 kg, Temperature 232 °C |
2.0 - 7.0 g/10 min @Load 11.0 lb, Temperature 450 °F |
ASTM D1238 |
Arkema Group KYNAR® EXAD 3000 Polyvinylidene Fluoride - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. Extrusion aid, lubricated. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanic.. |
|||
Melt Flow | 3.0 - 7.0 g/10 min @Load 2.16 kg, Temperature 280 °C |
3.0 - 7.0 g/10 min @Load 4.76 lb, Temperature 536 °F |
ASTM D1238 |
E-Polymers EFLEX® M100 Ethylene Octene Copolymer M-series: E-FLEX M series resins are a maleic anhydride grafted (MAH) polymer concentrate designed as synthetic rubber and polyolefin manufactured by E-Polymers. It offers excellent adhesion to nyl.. |
|||
Melt Flow | 3.0 - 7.0 g/10 min | 3.0 - 7.0 g/10 min | ASTM D1238 |
S&E Specialty Polymers GPP1001V0M-HCO PP Application: A polypropylene compound designed for injection molded industrial battery, electrical housing or appliance applications. It affords medium impact resistance with a high level of flam.. |
|||
Melt Flow | 2.0 - 7.0 g/10 min | 2.0 - 7.0 g/10 min | ASTM D1238 |
Polymer Resources PPX-GP5 Modified PPO, General Purpose with HDT of 270 F
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 6.0 - 7.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.0 - 7.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Granulate; ISO 1133/H |
SYNTHOS Krasten® 552M High Impact Polystyrene High impact grade with a wide range of Applications. Processed mainly by injection moulding. Production of consumer goods and technical parts subjected to increased mechanical stress. Good results i.. |