- Polymer Property : Melt Flow = 6.0 g/10 min
Polymer Property : Melt Flow = 6.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| PTS Tristar® PC-06 6 MFI Extrusion Grade Polycarbonate Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | (Condition L) ASTM D-1238-94a |
| Multibase Multi-Flex® TPO D-6206 This TPO product was developed for facia applications exhibiting adhesion for current automotive paint systems.Data provided by Multibase. |
|||
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
cm³/10 min |
| Polimeri Europa EDISTIR PD RK4514H High Impact Polystyrene (HIPS)
(discontinued **) Symbol according to ISO 1043-1: S/B Designation: Thermoplastic ISO 2897-SB,M,093-06-07-23 UL94 V-2, polybromodiphenylether (PBBE) free, antimony free, HIPS satisfying at 960°C the glow wire test.. |
|||
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| SABIC Innovative Plastics Lexan® FXG101 PC (Europe-Africa-Middle East) FXG101 is a Lexan PC Translucent Grade in our VisualFX Portfolio. The Grade was developed to meet the Aesthetic Differentiation requirements of today´s Customers. Color package may effect prope.. |
|||
| Melt Flow | 6.0 g/10 min @Temperature 240 °C |
6.0 g/10 min @Temperature 464 °F |
|
| Solvay Specialty Polymers Ixef® BXT-2000/0203 Polyarylamide (PARA)
(Unverified Data**) Ixef BXT-2000/0203 resin was developed specifically for extrusion and blow-molding processes. Unlike grades targeted for injection molding, Ixef BXT-2000/0203 resin can be successfully extruded into.. |
|||
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Kingfa FRHIPS-113 Flame Retardant Polystyrene Features:UL 94 V-0 @ 1.6 & 3.2mmExcellent balance properties, high strengthExcellent heat stabilityExcellent electrical propertiesApplications:Injection moldingGas moldingTV & Audio housingElectrica.. |
|||
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| LG Chemical LI951 Heat Resistant ASA Description: High Heat ASAApplication: Automotive Part (Radiator Grill, Side Mirror)CAS: 26299-47-8Information provided by LG Chemical |
|||
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| KKPC KOSYN KTR 201 Thermoplastic Elastomer (TPE) Thermoplastic Elastomer (TPE)Characteristics: KOSYN KTR101 is linear block copolymer made by solution polymerization which polymerizes butadiene and styrene in organic solvent. It is thermoplastics .. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| IRPC Polimaxx Polene 2363LC Polypropylene Block Copolymer CHARACTERISTICS: CONTAIN UV STABILIZER ADDITIVE, HIGH IMPACTAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES, FURNITURES, CRATES |
|||
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| LG Chemical LG-503 Styrene-Butadiene-Styrene Description: Linear structure, Non-Oil Extended Grade Thermoplastic ElastomerApplication: Asphalt Modifier, Plastic Modifier, Compounding, Adhesives etcCAS No. 9003-55-8Information provided by LG Ch.. |
|||
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® SP-0180 ABS, Unreinforced Extrusion Grade Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | 6.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
6.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM Data |
| Styron Magnum™ 348 ABS, Low Gloss MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM .. |
|||
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133; ASTM D1238 |
| Styron CALIBREâ„¢ 300-6 Polycarbonate Resin Overview: CALIBREâ„¢ 300-6 polycarbonate resin offer exceptional impact resistance, heat distortion resistance, and optical clarity as high melt strength for blow molding and sheet applications. .. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ ABPP-05 Antiblock Concentrate DescriptionPOLYBATCH® ABPP-05 Antiblock is an antiblock concentrate containing 5% synthetic silica based in homopolymer polypropylene. This masterbatch is designed to provide high clarity, low haz.. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Unipetrol PP MONSTEN® GB 506 Polypropylene Impact Copolymer Applications include injection molding and thermoforming. Basic stabilization. Impact copolymer.Information provided by Unipetrol RPA |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ White LL8970 TS Concentrate Based In LLDPE DescriptionPOLYBATCH® LL8970 TS is a general purpose white color concentrate containing 70% TiO2 based in LLDPE. POLYBATCH® LL8970 TS has been designed to provide color and opacity with good disp.. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ White LL8970 TS Concentrate Based In LLDPE DescriptionPOLYBATCH® LL8970 TS is a general purpose white color concentrate containing 70% TiO2 based in LLDPE. POLYBATCH® LL8970 TS has been designed to provide color and opacity with good disp.. |
|||
| Melt Flow | 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C |
6.0 g/10 min @Load 47.6 lb, Temperature 374 °F |
ISO 1133 |
| Total HDPE MS201 BN-NA High Density Polyethylene - Fuel Tank Resin Polyethylene: High molecular weight, high density fuel tank resin.Characteristics:Good melt strengthGood impact and creep resistanceExcellent stress cracking resistanceGMP.PE.062 certification.Appl.. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ ABPP-05 Antiblock Concentrate DescriptionPOLYBATCH® ABPP-05 Antiblock is an antiblock concentrate containing 5% synthetic silica based in homopolymer polypropylene. This masterbatch is designed to provide high clarity, low haz.. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Blue 40567 Concentrate Based In LDPE DescriptionPOLYBATCH® 40567 is a blue color concentrate based in LDPE. This concentrate was designed to provide opacity and color in polyolefin film and molding applications. POLYBATCH® 40567 is.. |
|||
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| A. Schulman POLYFORT™ FPP 1236 Glass Filled Chemically Coupled Homopolymer Polypropylene DescriptionPolyfort® FPP 1236 is a 20% glass filled chemically coupled homopolymer polypropylene product. Information provided by A. Schulman. |
|||
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene DescriptionPolyflam® RPP 1133 is a 30% glass filled, flame retardant copolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Melt Flow | 6.0 - 12 g/10 min @Temperature 230 °C |
6.0 - 12 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
| A. Schulman PP 1349 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1349 is a medium impact copolymer polypropylene.Information provided by A. Schulman. |
|||
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Cossa Polimeri ESTACARB 0501 Polycarbonate Polycarbonate for injection or extrusionHigh impact resistanceInformation provided by Cossa Polimeri S.r.l. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238, ISO 1133 |
| DuPont™ Elvax® 3175LGA Ethylene Vinyl Acetate DuPont™ Elvax® 3175LGA is an extrudable ethylene-vinyl acetate copolymer resin containing low gel material available in pellet form for use in conventional extrusion equipment designed to process .. |
|||
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Aclo Accutech Polypropylene Homopolymer HP0334T30L Talc Reinforced |
|||
| Melt Flow | 6.0 - 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 - 10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| AKG Polymers Vision PP PPC BL0806 Polypropylene Copolymer Compound Vision consists of a complete assortment of high-quality compounds based on industrial PP waste.Applications: Automotive, Non-food packaging, Storage/transport systems, Road and hydraulic Engineerin.. |
|||
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Polyram RamOfin PPC370B73 Polypropylene, 73% Mineral Filled 73% mineral filled polypropylene for heavy density injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||