Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 41 g/10 min @Load 5.00 kg, Temperature 260 °C |
41 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
Lanxess Durethan® BG 30 X 000000 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers/glass spheres, good surface, low warpage |
|||
Melt Flow | 41 g/10 min @Load 2.16 kg, Temperature 250 °C |
41 g/10 min @Load 4.76 lb, Temperature 482 °F |
Calculated from MVR using melt density; ISO 1133 |
Lanxess Pocan® B 7375 000000 PBT, White Pigment PBT, 25% white pigments, injection molding, improved light reflection, low tendency to warp |
|||
Melt Flow | 41 g/10 min @Load 2.16 kg, Temperature 270 °C |
41 g/10 min @Load 4.76 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
Lanxess Pocan® KU 2-7205 000000 PBT PBT, non-reinforced, injection molding, extrusion, flame retardant |
|||
Melt Flow | 41 g/10 min @Load 5.00 kg, Temperature 270 °C |
41 g/10 min @Load 11.0 lb, Temperature 518 °F |
Calculated from MVR using melt density; ISO 1133 |
Lanxess Pocan® S 7926 000000 PBT PBT, non-reinforced, injection molding, extrusion, flame retardant, impact modified |
|||
Melt Flow | 41 g/10 min | 41 g/10 min | ASTM D1238 |
ExxonMobil Escorene™ UL 04028CC Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: UL 04028CC is a copolymer of ethylene and vinyl acetate.Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: No Thermal Stabilizer: Yes Applications: Hot.. |
|||
Melt Flow | 41 g/10 min @Load 2.16 kg, Temperature 230 °C |
41 g/10 min @Load 4.76 lb, Temperature 446 °F |
cm<sup>3</sup>/10min Melt Volume-flow Rate; ISO 1133 |
DSM Arnitel® EL250 TPC-ET Injection Molding |