Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 39 g/10 min | 39 g/10 min | (Condition L) ASTM D-1238 |
Multibase Multi-Flex® TPE A 7321 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Melt Flow | 39 g/10 min @Load 1.20 kg, Temperature 300 °C |
39 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics Lexan® HP1HF PC Very high flow, biocompatible polycarbonate for healthcare applications. EtO sterilizable. |
|||
Melt Flow | 39 g/10 min @Load 1.20 kg, Temperature 300 °C |
39 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics Lexan® HP1HF PC (Europe-Africa-Middle East) Very high flow, biocompatible polycarbonate for healthcare applications. EtO sterilizable. |
|||
Melt Flow | 39 g/10 min @Load 1.20 kg, Temperature 300 °C |
39 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics Lexan® ML3729 PC Excellent flow, UV stabilized, grade which contains a release agent to ensure easy processing. |
|||
Melt Flow | 39 g/10 min @Load 1.20 kg, Temperature 300 °C |
39 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
SABIC Innovative Plastics Lexan® HP1HF PC (Asia Pacific) Very high flow, biocompatible polycarbonate for healthcare applications. EtO sterilizable. |
|||
Melt Flow | 39 - 47 g/10 min @Load 2.16 kg, Temperature 190 °C |
39 - 47 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem PRB 4215 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
Melt Flow | 39 g/10 min @Load 2.16 kg, Temperature 250 °C |
39 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
SABIC Innovative Plastics Valox® SHF434HR PBT PBT, Super High Flow, 20% glass reinforced,hydrolytically resistant. |
|||
Melt Flow | 39 g/10 min @Load 5.00 kg, Temperature 280 °C |
39 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D 1238 |
SABIC Innovative Plastics Noryl GTX GTX8430W PPE+PA 30% Glass Reinforced PPE+PA Alloy. Typically used for automotive connectors.This data was supplied by SABIC-IP for the Americas region. |
|||
Melt Flow | 39 g/10 min @Load 8.70 kg, Temperature 190 °C |
39 g/10 min @Load 19.2 lb, Temperature 374 °F |
ASTM D1238 |
Lubrizol Estane® 2103-80PF Thermoplastic Polyurethane Elastomer Formerly PellethaneFeature: Film and profile resinAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in.. |
|||
Melt Flow | 39 g/10 min @Load 2.16 kg, Temperature 230 °C |
39 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
ExxonMobil Exxtral™ BMV 208 Performance Polyolefin Product Description: Polyolefin injection molding compound with very high flow, high stiffness, good low temperature impact resistance, and excellent processability for automotive exterior trim appl.. |
|||
Melt Flow | 39 g/10 min | 39 g/10 min | ISO 1133 D |
Asahi Kasei Tenac® 7054 Homopolymer Acetal Resin High-flow grade with high crystallization rate for higher productivity.Information provided by Asahi Kasei Corporation. |
|||
Melt Flow | 39 g/10 min @Load 2.16 kg, Temperature 275 °C |
39 g/10 min @Load 4.76 lb, Temperature 527 °F |
ISO 1133 |
BASF Ultradur S 4090 G4 LS High Speed BK15077 20% Glass Filled PBT |
|||
Melt Flow | 39 g/10 min @Load 2.16 kg, Temperature 250 °C |
39 g/10 min @Load 4.76 lb, Temperature 482 °F |
Calculated from Volume Flow Rate of 30 cm<sup>3</sup>/10min.; ISO 1133 |
DSM Arnite® T06 202 XL (T-X01151) PBT (European Grade) Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame .. |