SABIC Innovative Plastics Noryl GTX GTX8430W PPE+PA
| Category | Polymer , Thermoplastic , Polyester, TP , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl GTX GTX8430W PPE+PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass Reinforced PPE+PA Alloy. Typically used for automotive connectors.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.012 cm/cm @Thickness 3.20 mm |
0.0070 - 0.012 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 39 g/10 min @Load 5.00 kg, Temperature 280 °C |
39 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 179 MPa | 26000 psi | Nominal Stress, brk, Type I, 5 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 165 MPa | 23900 psi | Nominal Stress, yld, Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 3.0 % | 3.0 % | Nominal Strain, 5 mm/min; ASTM D 638 |
| Elongation at Yield | 3.0 % | 3.0 % | Nominal Strain, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 8.48 GPa | 1230 ksi | 5 mm/min; ASTM D 638 |
| Flexural Strength | 262 MPa | 38000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 8.68 GPa | 1260 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.850 J/cm @Temperature -30.0 °C |
1.59 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 0.900 J/cm @Temperature 23.0 °C |
1.69 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | 8.43 J/cm @Temperature -30.0 °C |
15.8 ft-lb/in @Temperature -22.0 °F |
ASTM D 4812 |
| 8.49 J/cm @Temperature 23.0 °C |
15.9 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 | |
| Impact Test | 6.00 J @Temperature -30.0 °C |
4.43 ft-lb @Temperature -22.0 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 104 µm/m-°C @Temperature -40.0 - 40.0 °C |
57.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 256 °C @Thickness 3.20 mm |
493 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C @Thickness 3.20 mm |
464 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Vicat Softening Point | 244 °C | 471 °F | Rate B/50; ASTM D 1525 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1105-7995 PEEK, with carbon fiber
- Kolon KOPA® KN173HI3R High Impact Nylon 6
- SGL Carbon Group EK 200 Graphite
- Shinil Chemical SHINFLAME PC/ABS/GF Flame Retardant Polymer Housing
- Techmer ES HiFill® POM CO GF5 CC 5% Glass Filled
- SABIC Innovative Plastics NORYL GTX GTX987 PPE+PA66 (Asia Pacific)
- A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT
- ExxonMobil LL 6407.67 Injection Molding Resin
- DuPont Teijin Films Mylar® A Polyester Film, 48 Gauge
- Zylog Hipolyene® 4955 T Thermoplastic Polyolefin & PP Compound
Copyright © lookpolymers.com All Rights Reserved