BASF Ultradur S 4090 G4 LS High Speed BK15077 20% Glass Filled PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultradur S |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultradur S 4090 G4 LS High Speed BK15077 20% Glass Filled PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % | 0.40 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 104 cm³/g | 104 cm³/g | Viscosity number |
| Linear Mold Shrinkage, Flow | 0.0039 cm/cm | 0.0039 in/in | ISO Data |
| Linear Mold Shrinkage, Transverse | 0.0076 cm/cm | 0.0076 in/in | ISO Data |
| Melt Flow | 39 g/10 min @Load 2.16 kg, Temperature 275 °C |
39 g/10 min @Load 4.76 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 100 MPa | 14500 psi | 5mm/min; ISO 527 |
| Elongation at Break | 2.2 % | 2.2 % | 5mm/min; ISO 527 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | 1mm/min; ISO 527 |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179 |
| 3.30 J/cm² @Temperature -30.0 °C |
15.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359 |
| Melting Point | 223 °C | 433 °F | 10 K/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
IEC 60250 | |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 |
| 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 450 V | 450 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK15077 | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- RheTech Products P250-01 Polypropylene Copolymer, Black
- Pacific Sintered Materials BZ-111-U Yellow Brass Powdered Metal
- 3M Dyneon™ PFA 6503 C EPC Perfluoroalkoxy Fluorothermoplastic (discontinued **)
- Gouda Vuurvast VIBRON 150 G RAPID Dense Vibrating Refractory Castable
- Schott Glass 8688 Borosilicate Glass
- Techmer ES HiFill FR® PP FR-N X BKN001
- A. Schulman POLYBATCH™ Metallic Grey 80330/2
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 60 PHR Non-Black, Precipitated Calcium Carbonate
- 3M Scotchlite™ 680CR-14 Removable Reflective Graphic Film with Comply™ Adhesive
- Arkema Group KYNAR® 740-02 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
Copyright © lookpolymers.com All Rights Reserved