- Polymer Property : Melt Flow = 2.7 g/10 min
Polymer Property : Melt Flow = 2.7 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 2.7 g/10 min | 2.7 g/10 min | (Condition L) ASTM D-1238-94a |
| Multibase Multi-Flex® TPO 1047 (AH) The burn rate is 0.53 in/min; ASTM FM VSS 302.Data provided by Multibase. |
|||
| Melt Flow | 2.7 g/10 min | 2.7 g/10 min | Condition 230/2-8; ASTM D1238 |
| Plaskolite Optix® CA-82 General Purpose Acrylic Resin Injection Molding Grade Pellets. Highest Molecular Weight, good heat resistance. Superior mold release. |
|||
| Melt Flow | 2.7 g/10 min | 2.7 g/10 min | Condition 230/2-8; ASTM D1238 |
| Plaskolite West Optix® CA-82 General Purpose Acrylic Resin Injection Molding Grade Pellets. Highest Molecular Weight, good heat resistance. Superior mold release. |
|||
| Melt Flow | 2.7 - 6.4 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.7 - 6.4 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A; ASTM D1238 |
| PolyOne Maxxam™ PP CS 75 Polypropylene, Unspecified (PP, Unspecified) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Polimeri Europa Clearflex® CL 508 Octene Copolymer Linear Medium Density Polyethylene Clearflex CL 508 is an octene copolymer linear medium density polyethylene (C8-LMDPE), with antioxidants, suitable for cast film extrusion.Films manufactured with Clearflex CL 508 exhibit a good bal.. |
|||
| Melt Flow | 2.7 g/10 min @Load 5.00 kg, Temperature 190 °C |
2.7 g/10 min @Load 11.0 lb, Temperature 374 °F |
Procedure A; ASTM D1238 |
| PolyOne Elastamax™ EG-9182 Thermoplastic Elastomer (TPE) The Elastamax™ EG 9100 Series is a new family of olefin-based TPE compounds offering outstanding elastomeric performance in a lightweight and easy to process material. The EG 9100 Series of compoun.. |
|||
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
Procedure A; ASTM D1238 |
| PolyOne Maxxam™ FR PE 152 Polyethylene, Unspecified (PE, Unspecified) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
| Melt Flow | 2.7 - 3.3 g/10 min @Load 2.61 kg, Temperature 190 °C |
2.7 - 3.3 g/10 min @Load 5.75 lb, Temperature 374 °F |
ASTM D1238 |
| LG Chemical SEETEC BC500 LDPE Good Processability and Good electrical properties. Main Application: Cable insulationCAS No. 9002-88-4Information provided by LG Chemical |
|||
| Melt Flow | 2.7 - 3.3 g/10 min @Load 2.61 kg, Temperature 190 °C |
2.7 - 3.3 g/10 min @Load 5.75 lb, Temperature 374 °F |
ASTM D1238 |
| LG Chemical SEETEC BF500 LDPE Characteristics: Good Processability and Good Optical Properties Additives: Antiblocking Agent, Slip AgentApplications: Industrial Film & Food PackageCAS No. 9002-88-4Information provided by LG Chem.. |
|||
| Melt Flow | 2.7 - 3.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.7 - 3.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
| Ipiranga Petrochem PH 0361 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
| Melt Flow | 2.7 g/10 min @Load 6.60 kg, Temperature 337 °C |
2.7 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
| SABIC Innovative Plastics Ultem 3451 PEI (Asia Pacific) 45% Glass fiber and mineral filled, standard flow Polyetherimide (Tg 217C) with enhanced dimensional stability. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Melt Flow | 2.7 g/10 min @Load 6.60 kg, Temperature 295 °C |
2.7 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D1238 |
| SABIC Innovative Plastics ULTEM 8015 PEI High flow Polyetherimide blend. Meets FAR 25.853 and OSU 100/100 with low toxicity, smoke, and flame evolution. ECO Conforming. |
|||
| Melt Flow | 2.7 g/10 min @Load 6.60 kg, Temperature 295 °C |
2.7 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D1238 |
| SABIC Innovative Plastics ULTEM 8015 PEI (Asia Pacific) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 100/100 with low toxicity, smoke, and flame evolution. ECO Conforming. |
|||
| Melt Flow | 2.7 g/10 min @Load 21.6 kg, Temperature 150 °C |
2.7 g/10 min @Load 47.6 lb, Temperature 302 °F |
ASTM D1238 |
| Solvay Specialty Polymers Cogegum® AFR/760 Polyolefin Cogegum® HFFR -Halogen Free Fire Retardant compound. Polyolefin based thermoplastic compound containing a fire retardant system that contributes to give the cable self-extinguish properties with.. |
|||
| Melt Flow | 2.7 g/10 min @Load 5.00 kg, Temperature 280 °C |
2.7 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| SABIC Innovative Plastics NORYL PX138H PPE+HIPS (Asia Pacific) Modified PPO Resin with 20% Glass Fibre Reinforced |
|||
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Westlake Tymax™ GT7058 Anhydride Modified Acrylate Copolymer Westlake GT7058 is an anhydride modified acrylate copolymer designed for blown film extrusion that contains no slip and no antiblock additives. This resin is designed to function as a coextruded tie.. |
|||
| Melt Flow | 2.7 g/10 min | 2.7 g/10 min | |
| UBE UBEPOL BR15H HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %) Description: UBEPOL-BR15H is a in-between polymer of UBEPOL-BR15HB and UBEPOL-BR15HL.Information provided by UBE. |
|||
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238, ISO 1133 |
| DuPont™ Bynel® 41E710 Anhydride Modified LLDPE BYNEL® Series 4100 resins are anhydride-modified, linear low-density polyethylene (LLDPE) resins. All 4100 series resins are available in pellet form for use in conventional extrusion and coextrusi.. |
|||
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| ExxonMobil PP4792E1 Polymer Grade for Oriented Film Product Description: Easy processing grade primarily for oriented film applications.Availability: North America Features:MetalizableUses: Oriented FilmPackagingTapeProcessing Method: Film Extrusi.. |
|||
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
cm<sup>3</sup>/10min Melt Volume-flow Rate; ISO 1133 |
| DSM Arnitel® XG5855 TPC-ET Extrusion Grade |
|||
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Braskem EB 853/72 LDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Lamination film; general purpose; automatic packaging of solids products (FFS). Informatio.. |
|||
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Braskem EB853/72 Blown Film Extrusion Low Density Polyethylene Automatic packaging for several products; High transparency films.Additives: Antiblock, DInformation provided by Braskem. |
|||
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Braskem Green PE SLL318 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene Description: SLL118 is a Linear Low Density Polyethylene, copolymer of butene-1. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good process.. |
|||
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
| Braskem LF320 LLDPE Cast Film Extrusion Polyethylene Copolymer LF320 is a linear low-density polyethylene, copolymer of butene-1, produced by the gas phase process. It was developed for cast film extrusion. Films obtained with this product show a good processin.. |
|||
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
| Braskem LL318 LLDPE Cast Film Extrusion Polyethylene Copolymer LL318 is a linear low-density polyethylene, copolymer of butene-1, produced by the Spherilene process. It was developed for cast film extrusion. Films obtained with this product show good mechanical.. |
|||
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.7 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
| Braskem LL318 LLDPE Linear Low Density Extrusion Polyethylene LL318 is a linear low-density polyethylene, copolymer of butene-1, produced by the Spherilene process. It was developed for cast film extrusion. Films obtained with this product show good mechanical.. |
|||
| Melt Flow | 2.7 - 4.9 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.7 - 4.9 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| BASF Ecoflex® F BX 7011 Biodegradable Plastic A flexible plastic designed for film extrusion and extrusion coating. Ecoflex F BX 7011 comes closer than any other biodegradable plastic to the processing properties of LDPE and LLDPE. Blown film e.. |
|||
| Melt Flow | 2.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Braskem EB 853 LDPE Cast Film Extrusion Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Films for absorbents and diapers (with HDPE and LLDPE); general purpose. Information provi.. |
|||
| Melt Flow | 2.7 g/10 min | 2.7 g/10 min | Condition G |
| Ineos Nova 5100 High Impact Polystyrene
(discontinued **) Good balance of toughness and rigidity, USP Class VIApplications: Spools and reels, Thermoformed and molded packaging, Photographic cartridges, AppliancesProperties were determined on injection mold.. |
|||
| Melt Flow | 2.7 g/10 min | 2.7 g/10 min | Condition G |
| Ineos Nova 5620 High Impact Polystyrene
(discontinued **) High heat resistance, Good balance of toughness and rigidityApplications: Food service itemProperties were determined on injection molded specimens at 23°C and 50% R.H. unless otherwise specified.I.. |
|||