PolyOne Elastamax™ EG-9182 Thermoplastic Elastomer (TPE)

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	PolyOne Corporation
Trade Name	Elastamax™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Elastamax™ EG-9182 Thermoplastic Elastomer (TPE).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The Elastamax™ EG 9100 Series is a new family of olefin-based TPE compounds offering outstanding elastomeric performance in a lightweight and easy to process material. The EG 9100 Series of compounds feature unique high melt strength and shear thinning characteristics compared to conventional TPE materials for enhanced processability in extrusion applicationsInformation provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	0.878 g/cc	0.878 g/cc	ASTM D792
Melt Flow	2.7 g/10 min @Load 5.00 kg, Temperature 190 °C	2.7 g/10 min @Load 11.0 lb, Temperature 374 °F	Procedure A; ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	78	78	10 sec; ASTM D2240
	83	83	ASTM D2240
Tensile Stress	4.76 MPa @Strain 100 %	690 psi @Strain 100 %	510 mm/min; ASTM D412A
	5.24 MPa @Strain 200 %	760 psi @Strain 200 %	510 mm/min; ASTM D412A
	5.65 MPa @Strain 300 %	819 psi @Strain 300 %	510 mm/min; ASTM D412A
Tensile Strength, Yield	6.55 MPa	950 psi	510 mm/min; ASTM D412A
Elongation at Break	510 %	510 %	510 mm/min; ASTM D412A
Tear Strength	45.5 kN/m	260 pli	Die C, 510 mm/min; ASTM D624

Descriptive Properties	Value	Comments
Features	General Purpose
	Good Melt Strength
Forms	Pellets
Generic Material	TPE
Generic Name	Thermoplastic Elastomer (TPE)
Processing Method	Blow Molding
	Extrusion
	Foam Extrusion
	Profile Extrusion
	Sheet Extrusion
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Automotive Applications
	Construction Applications
	Consumer Applications
	General Purpose
	Industrial Applications