- Polymer Property : Melt Flow = 15 g/10 min
Polymer Property : Melt Flow = 15 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 10 - 15 g/10 min | 10 - 15 g/10 min | (Condition L) ASTM D-1238 |
| Multibase Multi-Flex® TPE A 7318 BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
| Melt Flow | 10 - 15 g/10 min | 10 - 15 g/10 min | (Condition L) ASTM D-1238 |
| Multibase Multi-Flex® TPE A 7318 GREY The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
| Melt Flow | 8.0 - 15 g/10 min | 8.0 - 15 g/10 min | (Condition L) ASTM D-1238 |
| Multibase Multi-Flex® TPE D 4210 BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
| Melt Flow | 5.0 - 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 - 15 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Plastcom PLASTALEN® PH 52 T 20 003/1M Polypropylene reinforced with 20% mineral filler PP homopolymer for injection molding with the content of 20 % mineral filler, heat stabilized. Application in automotive industry. Delivered in black grade.Information Provided by Plastcom spol. s r.. |
|||
| Melt Flow | 10 - 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 - 15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238/L |
| NIZHNEKAMSKNEFTEKHIM PP 1500N (F30G) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
| Melt Flow | 5.0 - 15 g/10 min | 5.0 - 15 g/10 min | ASTM D1238 |
| Polymer Resources PC/TP-GP1-[color]-3 PC Polyester, High Impact, Good Chemical Resistance, UV-stabilized Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Melt Flow | 5.0 - 15 g/10 min @Load 2.16 kg, Temperature 265 °C |
5.0 - 15 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| Polymer Resources PC/TP-GP1-UV PC/Polyester Alloy, UV-stabilized High Impact, Good Chemical Resistance, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information .. |
|||
| Melt Flow | 8.0 - 15 g/10 min | 8.0 - 15 g/10 min | ASTM D1238 |
| Polymer Resources TP-FR IM2 PBT, Impact Modified, Flame Retardant, High Flow Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Melt Flow | 8.0 - 15 g/10 min @Load 2.16 kg, Temperature 250 °C |
8.0 - 15 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources TP-FR-IM2 Polybutylene Terephthalate, Impact Modified, Flame Retardant, High Flow Polybutylene Terephthalate, Impact Modified, Flame Retardant, High FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test s.. |
|||
| Melt Flow | 5.0 - 15 g/10 min @Load 2.16 kg, Temperature 250 °C |
5.0 - 15 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources TP-IG30 Polybutylene Terephthalate, 30% Glass Reinforced, Reduced Warpage Polybutylene Terephthalate, 30% Glass Reinforced, Reduced WarpageProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.. |
|||
| Melt Flow | 5.0 - 15 g/10 min @Load 2.16 kg, Temperature 250 °C |
5.0 - 15 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources TP-IGFR-G30 Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant, Reduced Warpage Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant, Reduced WarpageProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmen.. |
|||
| Melt Flow | 10 - 15 g/10 min @Load 2.16 kg, Temperature 250 °C |
10 - 15 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources TP-M30 Polybutylene Terephthalate, 30% Mineral Reinforced, Reduced Warpage Polybutylene Terephthalate, 30% Mineral Reinforced, Reduced WarpageProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sampl.. |
|||
| Melt Flow | 5.0 - 15 g/10 min | 5.0 - 15 g/10 min | ASTM D1238 |
| Polymer Resources PC/TP-GP1 PC Polyester, High Impact, Good Chemical Resistance
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Melt Flow | 14 - 15 g/10 min | 14 - 15 g/10 min | ASTM D1238 |
| Polymer Resources PC/ABS-GP1-[color]-3 PC Blend, General Purpose, UV-stabilized Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Melt Flow | 5.0 - 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
5.0 - 15 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Polymer Resources PC-HM-FR1-[color]-TFE Polycarbonate, 10% Glass Reinforced, PTFE, Flame Retardant, Wear Resistant Polycarbonate, 10% Glass Reinforced, PTFE, Flame Retardant, Wear ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, tes.. |
|||
| Melt Flow | 10 - 15 g/10 min | 10 - 15 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Fiberfil® PP-62/CC/20/UV Polypropylene Copolymer, 20% Calcium Carbonate, UV Stabilized Information provided by FIBERFIL Engineered Plastics |
|||
| Melt Flow | 5.0 - 15 g/10 min @Load 2.16 kg, Temperature 150 °C |
5.0 - 15 g/10 min @Load 4.76 lb, Temperature 302 °F |
|
| Taiwan Sheen Soon Sheenthane® AH-620 TPU for Hotmelt Adhesive Thermoplastic polyurethane elastomer for hard hotmelt adhesiveExcellent bonding strength for polyester, TPU, nylon, PVC, leather, fabrics, etc. Melt flow may be customized. Used for hot melt adhes.. |
|||
| Melt Flow | 5.0 - 15 g/10 min @Load 2.16 kg, Temperature 150 °C |
5.0 - 15 g/10 min @Load 4.76 lb, Temperature 302 °F |
|
| Taiwan Sheen Soon Sheenthane® AH-670 TPU for Hotmelt Adhesive Thermoplastic polyurethane elastomer for hard hotmelt adhesiveExcellent bonding strength for polyester, TPU, nylon, PVC, leather, fabrics, etc. Melt flow may be customized. Used for hot melt adhes.. |
|||
| Melt Flow | 10 - 15 g/10 min | 10 - 15 g/10 min | ASTM D1238 |
| A. Schulman POLYFORT™ PP 1329 Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1329 is a medium impact copolymer polypropylene, available in matched automotive colors. Information provided by A. Schulman. |
|||
| Melt Flow | 8.0 - 15 g/10 min | 8.0 - 15 g/10 min | ASTM D1238 |
| A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible.. |
|||
| Melt Flow | 10 - 15 g/10 min | 10 - 15 g/10 min | ASTM D1238 |
| A. Schulman POLYFORT™ PP 1329 Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1329 is a medium impact copolymer polypropylene, available in matched automotive colors. Information provided by A. Schulman. |
|||
| Melt Flow | 8.0 - 15 g/10 min | 8.0 - 15 g/10 min | ASTM D1238 |
| A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible.. |
|||
| Melt Flow | 8.0 - 15 g/10 min | 8.0 - 15 g/10 min | ASTM D1238 |
| A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible.. |
|||
| Melt Flow | 13 - 15 g/10 min | 13 - 15 g/10 min | Cond L; ASTM D1238 |
| Washington Penn PPH4CF1 Polypropylene, 10% Calcium Carbonate Filled UV Stabilized; Injection molding grade.Applications: High flow for thin wall parts requiring long-flow. Wash tubs.Data provided by Washington Penn Plastic Co., Inc. |
|||
| Melt Flow | 8.0 - 15 g/10 min | 8.0 - 15 g/10 min | ASTM D1238 |
| A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible.. |
|||
| Melt Flow | 8.0 - 15 g/10 min | 8.0 - 15 g/10 min | ASTM D1238 |
| A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible.. |
|||
| Melt Flow | 12 - 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 - 15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| AKG Polymers Vision PP PPH BL1302 T20 Polypropylene Compound Vision consists of a complete assortment of high-quality compounds based on industrial PP waste.Applications: Automotive, Non-food packaging, Storage/transport systems, Road and hydraulic Engineerin.. |
|||
| Melt Flow | 10 - 15 g/10 min | 10 - 15 g/10 min | ASTM D1238 |
| A. Schulman POLYFORT™ PP 1329 Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1329 is a medium impact copolymer polypropylene, available in matched automotive colors. Information provided by A. Schulman. |
|||
| Melt Flow | 10 - 15 g/10 min | 10 - 15 g/10 min | ISO 1133 |
| Beijing Ranger Chem BLUESTAR® 1120 PBT Can be used directly to produce cable sheathInformation provided by Beijing Ranger Chemical Co. |
|||
| Melt Flow | 5.0 - 15 g/10 min | 5.0 - 15 g/10 min | ASTM D1238 |
| Polymer Resources PC/TP-GP3 PC Polyester, High Impact, Superior Chemical Resistance
(Unverified Data**)&l Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||