Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | (Condition L) ASTM D-1238 |
Multibase Multi-Flex® TPE A 7606 GREY The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | |
DuPont Fusabond® MN494D Ethylene Octene Copolymer
(discontinued **) Typical Use: Nylon 6 toughenerNylon 6/6 toughenerAvailability: North AmericaInformation provided by DuPont. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | Condition E; ASTM D 1238 |
Chevron Phillips 5554-H LDPE High Clarity, Medium Impact Film Resin
(discontinued **) Resin Type: HomopolymerCharacteristics: Excellent Clarity, Good Impact Strength, Excellent Processability, Low Coefficient of Friction, Good SealabilityApplications:Bread Bag, Dry Goods Packaging, P.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont Bynel® 4003 Anhydride-Modified HDPE Adhesive Resin
(discontinued **) Bynel® Series 4000 resins are anhydride-modified, high-density polyethylene resins. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | Exxon Method |
ExxonMobil Escorene® LD-303 EVA Film Resin, Clarity, High Impact
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 3.8% vinyl acetate copolymer, clarity film resin. The low melt index and comonomer context of this resin help produce films with superior impact .. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | Exxon Method |
ExxonMobil Escorene® LD-334 EVA Film Resin, Clarity, High Impact
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 4.2% vinyl acetate copolymer, clarity film resin. The low melt index and comonomer context of this resin help produce films with superior impact .. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont™ Surlyn® 1601B Sodium Ionomer Resin for Blown and Cast Film
(discontinued **) Surlyn® 1601B is an ionomer resin available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins. Applications: Meat, poultry, se.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ISO 1133 |
Iran Petrochemical (PCC) Moplen EP-YS30RE Polypropylene Moplen EP-YS30RE is a heterophasic polypropylene copolymer designed for extrusion applications where smooth processability and a good balance of mechanical properties are required. Moplen EP-YS30RE.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ISO 1133 |
Solvay Specialty Polymers Polidan® TUX 100 Polyethylene, Crosslinked (XLPE) Polidan® TUX 100 is a high density crosslinkable polyethylene compound manufactured according to the Sioplas® process. It has been developed for the production of crosslinked pipes in a wide r.. |
|||
Melt Flow | 1.3 g/10 min @Load 5.00 kg, Temperature 280 °C |
1.3 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL HH180 PPE+PS Noryl* HH180 is a high heat, unfilled modified polyphenylene ether resin with a Vicat B/120 temperature of 185 deg C. Noryl HH180 is only available in color 80365. |
|||
Melt Flow | 1.3 g/10 min @Load 5.00 kg, Temperature 280 °C |
1.3 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
SABIC Innovative Plastics NORYL HH180 PPE+PS (Europe-Africa-Middle East) Noryl* HH180 is a high heat, unfilled modified polyphenylene ether resin with a Vicat B/120 temperature of 185 deg C. Noryl HH180 is only available in color 80365. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis Borcoat™ ME0420 Grafted Polyethylene Adhesive for Steel Pipe Coating Borcoat ME0420 is a maleic-anhydride grafted polyethylene polymer to be extruded on conventional LDPE extruders with flat die or crosshead and it has excellent adhesion to epoxy powder and the top c.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 235 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238R |
UBE UBESTA® 3035LU1 Rigid Piping Grade Nylon 12 Description: UBESTA contributes to the field of Utilities such as plastic pipe system evolutionary developed for gas industry. It is used for both burial and for rehabilitation of existing cast iron.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ExxonMobil Method |
ExxonMobil EXACT™ 3128 Plastomer for Blown Film Applications Product Description: Exact 3128 is an ethylene-based butene plastomer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. It is designed fro both monolayer and multilayer coextruded .. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil Exceed™ 1327ED Metallocene Polyethylene Resin (European Grade) Product Description: Exceed 1327ED is a metallocene ethylene-hexene copolymer. It produces films which have high modulus whilst retaining good toughness. Additionally, Exceed 1327ED is fully formula.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont™ Surlyn® 1601 Sodium Ionomer Resin for Blown and Cast Film Surlyn® 1601 is an ionomer resin available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins. Applications: Meat, poultry, sea.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
condition E; ASTM D1238 |
DuPont™ Surlyn® 9120 Ionomer Resin, Zinc Surlyn® 9120 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ExxonMobil Method |
ExxonMobil LD 302.32 High Clarity, High Impact Film Resin LD 302 Series films exhibit superior impact strength, good heat sealability, and good low temperature properties. Typical applications are frozen food packaging or other food packaging.Information .. |
|||
Melt Flow | 1.3 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.3 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Diamond Polymers ABSPC 8020 Very High Impact Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Dow AMPLIFY™ EA 100 Ethylene-ethyl Acrylate (EEA) AMPLIFY™ EA 100 Functional Polymer is produced via a high pressure reactor. It exhibits high flexibility and imparts low temperature toughness to a wide range of engineering resins. This polymer.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont™ Surlyn® 1901 Sodium Ionomer Resin for Blown and Cast Film Surlyn® 1901 is a sodium ionomer resin available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins. Applications: Meat, poultr.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
DuPont Performance Polymers Delrin® 100AF Acetal (POM)
(Unverified Data**) 20% Teflon® Fiber Filled High Viscosity Acetal Homopolymer with Low Wear and Low Friction Delrin 100AF is a high viscosity acetal homopolymer containing 20% Teflon PTFE fibers. It is designed for a.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ASTM D1238 |
Total PPC 4280W Polypropylene, Impact Copolymer ATOFINA 4280W polypropylene is a nucleated impact copolymer. 4280W has a low fluidity providing melt strength with excellent impact properties. It is nucleated for added stiffness and surface hard.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil LDPE LD 302.56 Low Density Polyethylene Resin Product Description: LD 302 resins are 3.5% vinyl acetate copolymer, high film resins. The combination of comonomer content and low melt index helps produce films which exhibit superior impact stren.. |
|||
Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
DuPont™ Surlyn® 1601B-2 Sodium Ionomer Resin for Blown and Cast Film
(discontinued **) Surlyn® 1601 B-2 is an ionomer resin available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins. Applications: Meat, poultry,.. |
|||
Melt Flow | 1.3 g/10 min | 1.3 g/10 min | ASTM D1238 |
Huntsman PE1403 EVA Film Extrusion
(discontinued **) 4% Vinyl Acetate EVA Copolymer, DMF listed and FDA compliantFeatures: High clarity film with good toughness and flexibility at low temperatures.Applications: Film extrusion: frozen food and general .. |
|||
Melt Flow | 1.3 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.3 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Styron PULSE™ EXT 100 PC/ABS Engineering Resin Overview: PULSE EXT 100 engineering resin has been designed to provide excellent processability, high heat resistance, and high impact strength at both room and low temperatures. PULSE EXT 100 engin.. |