Solvay Specialty Polymers Polidan® TUX 100 Polyethylene, Crosslinked (XLPE)

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Crosslinkable
Manufacturer Solvay Specialty Polymers
Trade Name Polidan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Polidan® TUX 100 Polyethylene, Crosslinked (XLPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polidan® TUX 100 is a high density crosslinkable polyethylene compound manufactured according to the Sioplas® process. It has been developed for the production of crosslinked pipes in a wide range of diameters and wall thickness.Features: Crosslinkable; Good Abrasion Resistance; Good Chemical Resistance; Good Crack Resistance; Good Strength; High Density; High ESCR (Stress Crack Resist.); High Heat Resistance; Specialty GradeUses: Fittings; Industrial Applications; Oil/Gas Applications; PipingAdditional Properties: Gel Content - EN 579 > 65 %Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 0.955 g/cc
0.0345 lb/in³
ASTM D792
Melt Flow 1.3 g/10 min
1.3 g/10 min
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 6.00 MPa

@Temperature 100 °C
 870 psi

@Temperature 212 °F
 50 mm/min; ISO 527-2
26.0 MPa

@Temperature 23.0 °C
 3770 psi

@Temperature 73.4 °F
 50 mm/min; ISO 527-2
47.0 MPa

@Temperature -40.0 °C
 6820 psi

@Temperature -40.0 °F
 50 mm/min; ISO 527-2
Elongation at Break 110 %

@Temperature 23.0 °C
 110 %

@Temperature 73.4 °F
 ISO 527-2
170 %

@Temperature 100 °C
 170 %

@Temperature 212 °F
 ISO 527-2
390 %

@Temperature 150 °C
 390 %

@Temperature 302 °F
 ISO 527-2
Elongation at Yield 7.0 %

@Temperature -40.0 °C
 7.0 %

@Temperature -40.0 °F
 Type 1B, 50 mm/min; ISO 527-2
8.0 %

@Temperature 23.0 °C
 8.0 %

@Temperature 73.4 °F
 Type 1B, 50 mm/min; ISO 527-2
16 %

@Temperature 100 °C
 16 %

@Temperature 212 °F
 Type 1B, 50 mm/min; ISO 527-2
Tensile Modulus 0.130 GPa

@Temperature 100 °C
 18.9 ksi

@Temperature 212 °F
 1 mm/min; ISO 527-2
1.25 GPa

@Temperature 23.0 °C
 181 ksi

@Temperature 73.4 °F
 1 mm/min; ISO 527-2
3.30 GPa

@Temperature -40.0 °C
 479 ksi

@Temperature -40.0 °F
 1 mm/min; ISO 527-2
Flexural Modulus 0.167 GPa

@Temperature 100 °C
 24.2 ksi

@Temperature 212 °F
 ISO 178
2.60 GPa

@Temperature -40.0 °C
 377 ksi

@Temperature -40.0 °F
 ISO 178
Charpy Impact, Notched 1.50 J/cm²

@Temperature -40.0 °C
 7.14 ft-lb/in²

@Temperature -40.0 °F
 Type 1, Edgewise; ISO 179
NB

@Temperature 100 °C
 NB

@Temperature 212 °F
 Type 1, Edgewise; ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C

@Temperature -90.0 - -30.0 °C
 55.6 µin/in-°F

@Temperature -130 - -22.0 °F
 3
140 µm/m-°C

@Temperature -100 - 100 °C
 77.8 µin/in-°F

@Temperature -148 - 212 °F
 3
190 µm/m-°C

@Temperature -30.0 - 90.0 °C
 106 µin/in-°F

@Temperature -22.0 - 194 °F
 3
Vicat Softening Point 88.0 °C
190 °F
ISO 306
Descriptive Properties Value Comments
Agency Ratings ISO 9080 PE 100; ISO/DIS 12162 - MRS 10 Mpa
PE100; KTW
Availability Asia Pacific
Europe
North America
Processing Technique Extrusion; Injection Molding; Pipe Extrusion