Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.10 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
0.10 - 5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Polymer Resources ABS-G10 ABS, 10% Glass Reinforced Acrylonitrile Butadiene Styrene, 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information.. |
|||
Melt Flow | 0.10 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
0.10 - 5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Polymer Resources ABS-G30 ABS, 30% Glass Reinforced Acrylonitrile Butadiene Styrene, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information.. |
|||
Melt Flow | 0.10 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
0.10 - 5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Polymer Resources ABS-G5 ABS, 5% Glass Reinforced Acrylonitrile Butadiene Styrene, 5% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information .. |
|||
Melt Flow | 0.10 - 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.10 - 0.60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Ravago Manufacturing Americas Echo® RPEHD NAT Recycled HDPE Recycled High Density Polyethylene, Natural Color, Fractional Melt FlowInformation provided by Ravago. |
|||
Melt Flow | 0.10 - 4.0 g/10 min @Load 11.6 kg, Temperature 250 °C |
0.10 - 4.0 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
Polymer Resources PPX-GP6 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 290F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
Melt Flow | 0.10 - 4.0 g/10 min @Load 11.6 kg, Temperature 250 °C |
0.10 - 4.0 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
Polymer Resources PPX-GP7 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 300F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
Melt Flow | 0.10 g/10 min | 0.10 g/10 min | I<sub>2</sub>; ASTM D1238 |
Petromont 4100 High Density Polyethylene Resin Petromont HDPE 4100 is a high density polyethylene copolymer resin produced using the UNIPOL®
Process. This resin is designed for general use in large diameter heavy duty and non pressure pipe
appl.. |
|||
Melt Flow | 0.10 g/10 min | 0.10 g/10 min | I<sub>2</sub>; ASTM D1238 |
Petromont 5001 High Density Polyethylene Resin Petromont HDPE 5001 is a high-density polyethylene copolymer resin produced using the UNIPOL®
Process. This resin is intended for use in prime sheet and thermoforming applications such as arena boa.. |
|||
Melt Flow | 0.10 g/10 min | 0.10 g/10 min | I<sub>2</sub>; ASTM D1238 |
Petromont 7000 Medium Density Polyethylene Resin Petromont HDPE 7000 is a medium-density polyethylene hexene modified resin with an excellent balance of chemical resistance and durability. It is readily processed by blown sheet or flat die extrusi.. |
|||
Melt Flow | 0.10 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
0.10 - 5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Polymer Resources ABS-G15 ABS, 15% Glass Reinforced Acrylonitrile Butadiene Styrene, 15% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information.. |
|||
Melt Flow | 0.10 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
0.10 - 5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Polymer Resources ABS-G20 ABS, 20% Glass Reinforced Acrylonitrile Butadiene Styrene, 20% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information.. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
Condition E; ASTM D1238 |
Formosa Plastics Formolene® HP5221 Pipe HDPE
(discontinued **) High Density Hexene Copolymer Formolene® HP5221 is a high performance copolymer that is designed for the most demanding requirements of corrugated pipe applications. Formolene® HP5221 meets the re.. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
Condition E; ASTM D1238 |
Global GA-3245 High Density Polyethylene, Film Extrusion Grade
(discontinued **) Description-opacity, medium high stiffness, good impact strength, good chemical resistanceApplications- shopping bags, packing bagsInformation provided by Global Polymers Corporation. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
LyondellBasell Lupolen® 5361 A HDPE, Blow Molding Grade Easy-to-process blow molding grade for stackable canisters (up to 60 l), used for packing surface-active liquids, laundry and dishwashing detergents, disinfectants, drums (up to 220 l) for various s.. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
Condition E; ASTM D1238 |
Global GG-3245 High Density Polyethylene, Blow Molding Grade Description-opacity, medium high stiffness, good impact strength, good chemical resistanceApplications- auto parts, bottles, housewares, drums, containers, bottlesInformation provided by Global Poly.. |
|||
Melt Flow | 0.10 - 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.10 - 0.15 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
LG Chemical SEETEC PH150 HDPE Blown Film Grade Features: Characteristics : Excellent weather resistance & Environmental stress cracking resistanceAdditives : Anti-Oxidants, LubricantsProcessing recommendations : Maintain the stock temperature 20.. |
|||
Melt Flow | 0.10 g/10 min | 0.10 g/10 min | |
JPJ Technologies 6380M HDPE Extrusion Information provided by JPJ Technologies |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 446 °F |
|
Kuraray SEPTON® S45 Soft Compound Description: SEPTON® is a series of high performance thermoplastic rubbers developed by Kuraray Co. Ltd. using its unique isoprene technology. SEPTON® resins are a series of hydrogenated styre.. |
|||
Melt Flow | 0.10 g/10 min @Load 3.80 kg, Temperature 230 °C |
0.10 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Techmer ES Plastiblend® ABS 8004 UV MB Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Good UV Resistance and High Heat ResistanceTPCI# 6816121Information provided by TP Composites, Inc. |
|||
Melt Flow | 0.10 g/10 min @Load 3.80 kg, Temperature 230 °C |
0.10 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Techmer ES Plastiblend® ABS 8012 Availability: North AmericaForms: PelletsProcessing Method: ExtrusionInformation provided by TP Composites, Inc. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis FR4810 Low Smoke Zero Halogen Flame Retardant Jacketing Compound FR4810 is a thermoplastic, low smoke zero halogen (LSZH) flame retardant, black jacketing compound combining with flexibility and exceptional fluid resistance. The composition is based on the elemen.. |
|||
Melt Flow | <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
<= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil Paxon™ BA50-100 Blow Molding Resin Product Description: BA50-100 is a high molecular weight, high density polyethylene copolymer. This resin has superior stress crack resistance, high impact strength and good rigidity.Availability: .. |
|||
Melt Flow | <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
<= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil Paxon™ BA50-120 High Density Polyethylene Resin Product Description: BA50-120 is a high molecular weight, high density polyethylene copolymer. This resin has superior stress crack resistance, high impact strength and good rigidity.Availability: .. |
|||
Melt Flow | <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
<= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil Paxon™ BA53-035 Blow Molding Resin
(discontinued **) BA53-035 is a high molecular weight, high density polyethylene copolymer offering an outstanding combination of stiffness and toughness. The resin provides superior melt strength and impact resista.. |
|||
Melt Flow | <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
<= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil Paxon™ BC50-100 Sheet Extrusion and Blow Molding Resin
(discontinued **) BC50-100 is a high molecular weight, high density polyethylene copolymer. This resin has superior stress crack resistance, high impact strength and good rigidity.Information provided by ExxonMobil .. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
E-Polymers EFLEX® S5070 Extrusion S-series ( SBS, SEBS compound resins): E-FLEX S series resins are based on SBS/SEBS/SEEPS/PP exhibiting excellent high and low temperature resistance and easy processing with conventional thermoplas.. |
|||
Melt Flow | <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
<= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil Paxon™ BA46-055 Blow Molding Resin Product Description: BA46-055 is a high molecular weight high density polyethylene copolymer. It possesses a combination of excellent processability, outstanding melt strength, high impact strength.. |
|||
Melt Flow | 0.10 - 4.0 g/10 min | 0.10 - 4.0 g/10 min | ASTM D1238 |
Polymer Resources PPX-GP6 Modified PPO, General Purpose with HDT of 290 F
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 0.10 - 4.0 g/10 min | 0.10 - 4.0 g/10 min | ASTM D1238 |
Polymer Resources PPX-GP7 Modified PPO, General Purpose with HDT of 300 F
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 0.10 - 1.0 g/10 min | 0.10 - 1.0 g/10 min | |
Kazanorgsintez P2ES-12 Electrically Conductive Polyethylene Composite Production Method: P2ES-12 is produced from low density polyethylene, modified by carbon black, rubber and calcium stearate. Application: Designed for production of pipes used for explosive mate.. |