ExxonMobil Paxon™ BC50-100 Sheet Extrusion and Blow Molding Resin (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Paxon™ BC50-100 Sheet Extrusion and Blow Molding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BC50-100 is a high molecular weight, high density polyethylene copolymer. This resin has superior stress crack resistance, high impact strength and good rigidity.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.949 g/cc	0.0343 lb/in³	ASTM D4883
ESCR 100% Igepal®	>= 800 hour	>= 800 hour	ASTM D1693 Condition B
Melt Flow	10 g/10 min	10 g/10 min	190 / 21.6 (HLMI); ASTM D1238
	<= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C	<= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	26.2 MPa	3800 psi	ASTM D638
Elongation at Break	1000 %	1000 %	ASTM D638
Flexural Modulus	1.24 GPa	180 ksi	Method1, Procedure A (1"x3"x0.125"), Tangent calculation; ASTM D790
Tensile Impact Strength	252 kJ/m²	120 ft-lb/in²	ASTM D1822
	210 kJ/m² @Temperature -40.0 °C	100 ft-lb/in² @Temperature -40.0 °F	ASTM D1822

Thermal Properties	Metric	English	Comments
CTE, linear	120 µm/m-°C @Temperature 20.0 °C	66.7 µin/in-°F @Temperature 68.0 °F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	70.0 °C	158 °F	ASTM D648
Vicat Softening Point	121 °C	250 °F	ASTM D1525
Brittleness Temperature	<= -76.1 °C	<= -105 °F	ASTM D746

Processing Properties	Metric	English	Comments
Melt Temperature	204 °C	400 °F

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer