Nanocyl NANOCYL™ NC2101 Double-Wall Isolated and Bundled Carbon Nanotubes - Research Grade

Category Carbon
Manufacturer Nanocyl
Trade Name NANOCYL™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nanocyl NANOCYL™ NC2101 Double-Wall Isolated and Bundled Carbon Nanotubes - Research Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NANOCYL™ NC2000 series double-wall carbon nanotubes are produced via the catalytic carbon vapor deposition (CCVD) process. Nanotubes which exit the reactor are then purified to greater than 90% carbon to produce the 2100 grade. This grade is then functionalized with COOH to produce the 2101 grade. These products are available in 1 g to 1 kg order quantities.A primary interest is in applications requiring high field emission characteristics, transparency or high surface area.
Physical Properties Metric English Comments
Specific Gravity 1.30 - 2.00 g/cc
1.30 - 2.00 g/cc
Specific Surface Area >= 500 m²/g
>= 500 m²/g
BET
Mechanical Properties Metric English Comments
Tensile Strength 10000 - 60000 MPa
1.45e+6 - 8.70e+6 psi
Elongation at Break 10 %
10 %
Tensile Modulus 1000 GPa
145000 ksi
Thermal Properties Metric English Comments
Thermal Conductivity >= 3000 W/m-K
>= 20800 BTU-in/hr-ft²-°F
Component Elements Properties Metric English Comments
Carbon, C >= 90 %
>= 90 %
TGA
Electrical Properties Metric English Comments
Volume Resistivity 0.00001 - 0.0001 ohm-cm
0.00001 - 0.0001 ohm-cm
Descriptive Properties Value Comments
Average Diameter 3.5 nanometers
HRTEM
Average Length 1 to 10 microns
TEM/SEM
-COOH Functionalization <1%
XPS
Metal Oxide <10%
TGA