Kuraray SEPTON® A4 Hot Melt Adhesive

Category Polymer , Adhesive , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer Kuraray Company
Trade Name SEPTON®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kuraray SEPTON® A4 Hot Melt Adhesive.pdf
  Online Service   lookpolymers   27660005
Material Notes:
Description: SEPTON® is a series of high performance thermoplastic rubbers developed by Kuraray Co. Ltd. Using its isoprene technology. SEPTON® resins are a series of hydrogenated styrenic block copolymers, which exhibit rubber-like properties over a wide range of temperatures. SEPTON®'s characteristics include:Excellent Mechanical PropertiesGood WeatherabilityExcellent Low Temperature PropertiesExcellent Electrical PropertiesSuperior Heat ResistanceExcellent Chemical ResistanceLow ToxicitySEPTON® grades are available with a range of Shore A hardness of 35-95 and tensile strengths of 290-5600 psi. SEPTON® resins are highly extendible with fillers, resins and oils, which allows formulation of a variety of hardness for adhesives, sealants and various compounds. As an additive, SEPTON® resins can be used to improve toughness of a variety of plastics. Several SEPTON® grades have U.S. FDA and USP Class VI approval.SEPTON® has a versatile series of grades which can be used in numerous processing techniques such as blow molding, injection molding, extrusion, hot melt and solution coatings. SEPTON® resins are thermoplastics therefore, the scrap is recyclable without significant loss of properties.When blended with a tackifier and a process oil, SEPTON® polymers provide hot melt adhesives having excellent heat and weather resistance.SEPTON® Solubility: Partial to Non-Soluble in: Ethyl Acetate, MEK, Methanol, Ethanol, Acetone, WaterSoluble in: Petroleum Ether, Toluene, Benzene, Hexane and CyclohexaneTackifiers Compatible with SEPTON®:Rubber Phase: Acyclic Saturated Hydrocarbon resins, Hydrogenated Terpene resins, Petroleum resin and Hydrogenated Rosin resinStyrene Phase: Aromatic resins and Styrenic resinsFormulation (parts by weight): SEPTON® 2004 - 100, Acyclic Saturated Hydrocarbon Resin - 300, Paraffinic Process Oil - 100 Information provided by The Kuraray Group.
Physical Properties Metric English Comments
Brookfield Viscosity 4700 cP
4700 cP
melt viscosity
Mechanical Properties Metric English Comments
Peel Strength 0.490 kN/m
2.80 pli
to polyethylene, 180° peel test, rate of peel = 300mm/min at 25°C
1.354 kN/m
7.725 pli
to stainless steel, 180° peel test, rate of peel = 300mm/min at 25°C
Descriptive Properties Value Comments
Cohesion, Static Shear min 240
load: 1 kg at 40°C, sample size: 25 mm x 25 mm
Rolling Ball Tack Test 2 balls (Max)