DuPont Teijin Films Teijin® Tetoron® U2 Polyester Film, 1000 Gauge
| Category | Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film |
| Manufacturer | DuPont Teijin Films (DTF) |
| Trade Name | Teijin® Tetoron® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Teijin Films Teijin® Tetoron® U2 Polyester Film, 1000 Gauge.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Teijin® Tetoron® U2 is an opaque white polyester film. Teijin® Tetoron® U2 is available in the following variants:U2: Non-pretreated; available in 150, 200, 300, 400, 500 & 1000 gaugeU298W: Adhesion Pretreated (both sides); available in 750 & 1000 gaugeU2L98W: Low Shrinkage, Adhesion Pretreated (both sides); available in 500 gaugeTypical Applications: Prepaid cards (Magnetic Cards)LabelImagingInformation provided by DuPont.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 100 % | 100 % | ASTM D882A |
| 100 % | 100 % | U2L98W; ASTM D882A | |
| Film Elongation at Break, TD | 80 % | 80 % | ASTM D882A |
| 90 % | 90 % | U2L98W; ASTM D882A | |
| Film Tensile Strength at Break, MD | 136.96 MPa | 19865 psi | U2L98W; ASTM D882A |
| 156.96 MPa | 22765 psi | ASTM D882A | |
| Film Tensile Strength at Break, TD | 146.96 MPa | 21315 psi | U2L98W; ASTM D882A |
| 156.96 MPa | 22765 psi | ASTM D882A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 0.90 % @Temperature 150 °C, Time 1800 sec |
0.90 % @Temperature 302 °F, Time 0.500 hour |
Unrestrained, U2L98W |
| 1.0 % @Temperature 150 °C, Time 1800 sec |
1.0 % @Temperature 302 °F, Time 0.500 hour |
Unrestrained | |
| Shrinkage, TD | 0.00 % @Temperature 150 °C, Time 1800 sec |
0.00 % @Temperature 302 °F, Time 0.500 hour |
Unrestrained, U2L98W |
| 0.10 % @Temperature 150 °C, Time 1800 sec |
0.10 % @Temperature 302 °F, Time 0.500 hour |
Unrestrained |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 55 % | 55 % | 60°; ASTM D1003 |
| 55 % | 55 % | 60°, U2L98W; ASTM D1003 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | 0 | a |
| 0 | a, U2L98W | |
| -2.4 | b, U2L98W | |
| -2.7 | b | |
| 91.1 | L | |
| 91.1 | L, U2L98W |