Carpenter Extendo-Die® Hot Work Die Steel, Tempered 538°C (1000°F)
| Category | Metal , Ferrous Metal , Tool Steel , Air-Hardening Steel , Hot Work Steel |
| Manufacturer | Carpenter Technology Corporation (Cartech) |
| Trade Name | Extendo-Die® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Carpenter Extendo-Die® Hot Work Die Steel, Tempered 538°C (1000°F).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Carpenter Technology Corporation.This steel combines extreme toughness with good red hardness in large section sizes. This alloy may also be considered for many cold work applications where H13 is currently used, particularly in large section size applications. Extendo-Die® hot work die steel can be water cooled in service.Extendo-Die® is a registered trademark of Carpenter Technology Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.72 g/cc | 0.279 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 594 | 594 | Estimated from Rockwell C for 3000 kg load, 10 mm ball Brinell measurement. |
| Hardness, Knoop | 660 | 660 | Estimated from Rockwell C |
| Hardness, Rockwell C | 57 | 57 | |
| Hardness, Vickers | 632 | 632 | Estimated from Rockwell C |
| Tensile Strength, Ultimate | 2250 MPa | 326000 psi | |
| Tensile Strength, Yield | 1900 MPa @Strain 0.200 % |
276000 psi @Strain 0.200 % |
|
| Elongation at Break | 8.0 % | 8.0 % | |
| Reduction of Area | 28 % | 28 % |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.6 µm/m-°C @Temperature 24.0 - 93.0 °C |
5.89 µin/in-°F @Temperature 75.2 - 199 °F |
|
| 12.6 µm/m-°C @Temperature 427 - 788 °C |
7.00 µin/in-°F @Temperature 801 - 1450 °F |
||
| 13.1 µm/m-°C @Temperature 24.0 - 649 °C |
7.28 µin/in-°F @Temperature 75.2 - 1200 °F |
||
| Transformation Temperature | 857 °C | 1570 °F | Ac<sub>1</sub> |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.44 % | 0.44 % | |
| Chromium, Cr | 6.0 % | 6.0 % | |
| Iron, Fe | 89 % | 89 % | as remainder |
| Manganese, Mn | 0.45 % | 0.45 % | |
| Molybdenum, Mo | 1.9 % | 1.9 % | |
| Silicon, Si | 1.0 % | 1.0 % | |
| Sulfur, S | <= 0.0050 % | <= 0.0050 % | |
| Vanadium, V | 0.80 % | 0.80 % |