Polymer Property : Modulus of Elasticity = 30000 ksi Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Modulus of Elasticity	207 GPa @Temperature 100 Â°C	30000 ksi @Temperature 212 Â°F
Haynes 230Â® alloy plate, 4000 hours exposure at 649Â°C (1200Â°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Modulus of Elasticity	207 GPa @Temperature 100 Â°C	30000 ksi @Temperature 212 Â°F
Haynes 230Â® alloy, 10% cold reduction, 1177Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Modulus of Elasticity	207 GPa @Temperature 100 Â°C	30000 ksi @Temperature 212 Â°F
Haynes 230Â® alloy, 20% cold reduction, 1066Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Modulus of Elasticity	207 GPa @Temperature 100 Â°C	30000 ksi @Temperature 212 Â°F
Haynes 230Â® alloy, 20% cold reduction, 1177Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Modulus of Elasticity	207 GPa @Temperature 100 Â°C	30000 ksi @Temperature 212 Â°F
Haynes 230Â® alloy, 30% cold reduction, 1177Â°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Modulus of Elasticity	207 GPa	30000 ksi
Latrobe Graph-AirÂ® Cold Work Tool Steel (ASTM A10) Graph-Air tool steel is an air-hardening, graphitic tool steel with outstanding resistance to metal-to-metal sliding wear and galling. The steel contains a uniform dispersion of graphite particles w..
Modulus of Elasticity	207 GPa	30000 ksi
Latrobe DuraTechâ„¢ Xtreme Powder Metal Tool Steel DuraTech Xtreme tool steel is a medium-carbon, powder metallurgy tool steel which has an outstanding combination of properties including very high impact toughness, very good hot hardness, and good ..
Modulus of Elasticity	207 GPa	30000 ksi
Latrobe TNWâ„¢ ASTM M10 High Speed Steel TNW is an M10 type high speed steel with a composition that combines the high toughness of a high-molybdenum steel and the excellent wear resistance provided by the 2% vanadium content. TNW is popul..
Modulus of Elasticity	207 GPa	30000 ksi	Tension
Special Metals DURANICKELÂ® 301 (UNS N03301) Annealed and Aged Strip Tensile strength (ultimate), hardness, and elongation values reported here are typical for Annealed and Aged Strip specifically. Other property values are typical of aged DURANICKELÂ® alloy 301 or..
Modulus of Elasticity	207 GPa	30000 ksi	Tension
Special Metals DURANICKELÂ® 301 (UNS N03301) Annealed and Aged Wire Tensile strength (ultimate) and elongation values reported here are typical for Annealed and Aged Wire specifically. Other property values are typical of aged DURANICKELÂ® alloy 301 or the alloy i..
Modulus of Elasticity	207 GPa	30000 ksi	Tension
Special Metals DURANICKELÂ® 301 (UNS N03301) Spring Wire Tensile strength (ultimate) and elongation values reported here are typical for Spring Wire specifically. Other property values are typical of annealed DURANICKELÂ® alloy 301 or the alloy in gener..
Modulus of Elasticity	207 GPa	30000 ksi	Tension
Special Metals DURANICKELÂ® 301 (UNS N03301) Spring Wire, Aged Tensile strength (ultimate) and elongation values reported here are typical for Spring Wire, Aged specifically. Other property values are typical of aged DURANICKELÂ® alloy 301 or the alloy in gen..
Modulus of Elasticity	207 GPa	30000 ksi
Crucible Steel AIRKOOL® (AISI A2) Tool Steel Airkool (AISI A2) is an air-hardening medium alloy tool steel which is heat treatable to HRC 60-62. It has wear resistance intermediate between the oil hardening tool steels (O1) and the high carbon..
Modulus of Elasticity	207 GPa	30000 ksi
Crucible Steel CPM® REX® M35HCHS High Speed Steel, AISI M35 CPM REX M35HCHS is a 5% cobalt modification of M2 high speed steel used almost exclusively for hobs and other gear cutting tools where higher red hardness is required. Made by the Crucible Particle ..
Modulus of Elasticity	207 GPa	30000 ksi
Crucible Steel CRU-WEAR® Tool Steel CRU-WEAR is an air-hardening tool steel, heat treatable to HRC 60-65. Designed as an upgrade to D2, it offers better wear resistance, greater toughness and higher attainable hardness. Compared to th..
Modulus of Elasticity	207 GPa	30000 ksi
Crucible Steel PEERLESS A Tool Steel, AISI H21 Peerless A is designed for tools which will run hot, at operating temperatures between about 600F and 1100F. The tools should not be water cooled in service, due to a high risk of thermal shock. Pee..
Modulus of Elasticity	207 GPa	30000 ksi
Crucible Steel REX® M2 S High Speed Steel REX M2 is a tungsten-molybdenum high speed steel which gives outstanding performance in all operations where a general purpose high speed steel is required. REX M2 has a wide hardening range, excell..
Modulus of Elasticity	207 GPa	30000 ksi
Crucible Steel S7 (AISI S7) Tool Steel Crucible S7 is a shock resisting tool steel with excellent toughness and high strength, along with low to medium wear resistance. It has been widely used for many years to make chisels and punches w..
Modulus of Elasticity	207 GPa @Temperature 23.0 °C	30000 ksi @Temperature 73.4 °F
Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 732°C/8hr/FC to 621°C/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t..
Modulus of Elasticity	207 GPa	30000 ksi
ATI Allegheny Ludlum AL 22™ Nickel-Base Alloy, UNS N06022 AL 22 alloy is a Ni-Cr-Mo alloy that provides outstanding resistance to pitting, crevice corrosion, intergranular attack, and stress corrosion cracking. The combination of Cr, Ni, Mo, and W provide..
Modulus of Elasticity	207 GPa @Temperature 23.0 °C	30000 ksi @Temperature 73.4 °F
Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Cold Drawn 37.5% Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t..
Modulus of Elasticity	207 GPa @Temperature 23.0 °C	30000 ksi @Temperature 73.4 °F
Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Cold Drawn 37.5% Plus Aging 649°C (1200°F)/4hr/FC to 579°C/4hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t..
Modulus of Elasticity	207 GPa	30000 ksi
Crucible Steel S7 XL (Premium AISI S7) Tool Steel Crucible S7XL is a double refined, high purity grade of S7. The remelt operation produces a cleaner steel with a more uniform microstructure, offering the following advantages over conventional S7:B..
Modulus of Elasticity	207 GPa @Temperature 100 °C	30000 ksi @Temperature 212 °F
Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..
Modulus of Elasticity	207 GPa @Temperature 93.0 °C	30000 ksi @Temperature 199 °F
Haynes Hastelloy® C-4 alloy, welded plate 12.7 mm (1/2 in.) thick, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T..
Modulus of Elasticity	207 GPa	30000 ksi
Carpenter Hampden® High Carbon, High Chrome Tool Steel (Oil-Wear) (AISI D3) Hampden tool steel is an oil-hardening, high-carbon, high-chromium die steel having extreme wear resistance, It hardens with very little change in size or shape. Hampden tool steel is a deep-hardeni..
Modulus of Elasticity	207 GPa	30000 ksi
Schmolz + Bickenbach Thermodur® 2343 EFS Extra Fine Structure (H-11)- Hot Work Die Steel Description: Thermodur® 2343 is a single melt Extra Fine Structure (EFS) hot work die steel and Supplied in the annealed conditionCharacteristics: Good toughness; Moderate high-temperature strength..
Modulus of Elasticity	207 GPa	30000 ksi
Crucible Steel REX® M42 High Speed Steel, AISI M42 REX M42 is a super cobalt high speed steel which may be heat treated to HRC 68. This makes REX M42 outstanding for special purpose cutting tools, with requirements beyond the capability of general p..
Modulus of Elasticity	207 GPa	30000 ksi
Latrobe LSS™ A6 Tool Steel (ASTM A6) TLS A6 tool steel is a medium-alloy, air-hardening tool steel that is characterized by its ability to be through hardened while using the low austenitizing temperatures which are typically associate..
Modulus of Elasticity	207 GPa	30000 ksi
Latrobe LSS™ L6 Tool Steel (ASTM L6) TLS L6 tool steel is a versatile, oil-hardening tool steel that is characterized by very good toughness. TLS L6 tool steel is suitable for use as tools, dies, and machine parts which require a good ..