Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 23.0 °C |
1.00e+14 ohm-cm @Temperature 73.4 °F |
ASTM D257 |
DuPont Performance Polymers Crastin® 6130 NC010 PBT
(Unverified Data**) Crastin® 6130 NC010 is an unreinforced, medium high viscosity polybutylene terephthalate resin for extrusion and injection molding.Information provided by DuPont Performance Polymers |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 23.0 °C |
1.00e+14 ohm-cm @Temperature 73.4 °F |
DAM; ASTM D257 |
DuPont Performance Polymers Zytel® 105F BK010 Nylon 66
(Unverified Data**) Zytel® 105F BK010 is a lubricated, fast cycling, weather resistant PA 66 resin. Zytel® 105F BK010 contains finely dispersed carbon black.Information provided by DuPont Performance Polymers |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 25.0 °C |
>= 1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM-D257 |
CeramTec 665 Steatite, MgO•SiO2 Steatites used in place of aluminas are a cost-effective way to meet performance requirements. They are easier to form and fire at lower temperatures. 665 L533C has low dielectric loss. It makes exc.. |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 20.0 °C |
1.00e+14 ohm-cm @Temperature 68.0 °F |
IEC 672-1 |
CeramTec B 601 Alumina, 98.5% Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at elevated temperatures. |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 20.0 °C |
1.00e+14 ohm-cm @Temperature 68.0 °F |
IEC 672-1 |
CeramTec DN 70 Dispersion Ceramic, Al2O3-ZrO2 DN 70 is a ZTA Alumina Toughened Zirconia. |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 20.0 °C |
>= 1.00e+14 ohm-cm @Temperature 68.0 °F |
IEC 672-1 |
CeramTec Rubalit® IS 95 Alumina Rubalit® IS 95 is a high-performance alumina ceramic. Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at eleva.. |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 25.0 °C |
>= 1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM-D1829 |
CoorsTek AD-996 99.6% Alumina |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 25.0 °C |
>= 1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM-D1829 |
CoorsTek ADOS-90R 91% Alumina Thick Film Substrate This 91-percent alumina (nominal) formulation offers a dark brown body for special applications. Applications: thick films and lasers |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 25.0 °C |
>= 1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM-D1829 |
CoorsTek ADS-96R 96% Alumina Thick Film Substrate This high-purity material ensures strong, reliable performance for ceramic substrate application. Applications: thick films and lasers |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 100 °C |
>= 1.00e+14 ohm-cm @Temperature 212 °F |
ASTM-D257 |
CoorsTek ADS-995 99.5% Alumina Thin Film Applications: thin film substrates |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 100 °C |
>= 1.00e+14 ohm-cm @Temperature 212 °F |
ASTM-D257 |
CoorsTek ADS-996 99.6% Alumina Thin Film Applications: thin film substrates |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 25.0 °C |
>= 1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM-D1829 |
CoorsTek PlasmaPure-UC™ 99.9% Alumina |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 25.0 °C |
>= 1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM-D257 |
CoorsTek Superstrate® 996 99.6% Alumina Thin Film Applications: thin film substrates |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 100 °C |
>= 1.00e+14 ohm-cm @Temperature 212 °F |
ASTM-D257 |
CoorsTek Superstrate® 996 99.6% Alumina Thin Film Applications: thin film substrates |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 300 °C |
>= 1.00e+14 ohm-cm @Temperature 572 °F |
ASTM-D257 |
CoorsTek Superstrate® TPS 99.6% Alumina Thin Film Applications: thin film substrates |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 25.0 °C |
1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM D257 |
3M Scotchcast™ 265 Electrical Epoxy Powder Resin 3M Scotchcast Electrical Resin 265 is a new solution to an old problem. Historically, manufactures of coils, stators and armatures have used liquid-based varnishes or resins to coat and impregnate t.. |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 20.0 °C |
1.00e+14 ohm-cm @Temperature 68.0 °F |
|
Anderman Ceramics EA995 Sintered Alumina, 99.5% Densely sintered alumina is characterized by: high strength and hardness, temperature stability, electrical insulation, and high wear resistance and corrosion resistance even at high temperatures. .. |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 25.0 °C |
>= 1.00e+14 ohm-cm @Temperature 77.0 °F |
ASTM-D257 |
CeramTec 614/698 Alumina, 96% 614/698 (96%) is a high-strength alumina with good mechanical properties, as well as good wear and chemical resistance. It also features excellent electrical properties. 614 is white; 698 is pink. |
|||
Volume Resistivity | 1.00e+14 ohm-cm @Temperature 20.0 °C |
1.00e+14 ohm-cm @Temperature 68.0 °F |
IEC 672-1 |
CeramTec B 40 Alumina, 99.1% B 40 is the ideal sliding mate with the same properties as Rubalit® A 1896. It contains a larger share of Al2O3 for superior chemical stability. |
|||
Volume Resistivity | >= 1.00e+14 ohm-cm @Temperature 20.0 °C |
>= 1.00e+14 ohm-cm @Temperature 68.0 °F |
|
CeramTec Rubalit® A 1898 Alumina, 98% Rubalit® A 1898 (98%) was specifically developed in response to electrical and electronic engineering needs. In conjunction with CeramTec's complementary metallization systems, a vacuum-tight bond .. |