Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 8000 ohm-cm | 8000 ohm-cm | 35 parts per 100 of NC E1MY-02 in the final compound |
Nanocyl EPOCYL™ NC E1MY-02 Master Batch Liquid tetrafunctional epoxy Resin for non-Solvent Formulation Purposes EPOCYL™ NC E1MY-02 is a Mater Batch based on liquid tetrafunctional epoxy resin containing high concentration of Carbon Nanotubes (CNT) produced by Nanocyl. It is specifically developed to enhance.. |
|||
Volume Resistivity | 8000 ohm-cm | 8000 ohm-cm | |
LATI Larton L K/20 L-PPS, 20% Carbon Fiber Reinforced Linear Polyphenylene Sulfide (L-PPS) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle.. |
|||
Volume Resistivity | 8000 ohm-cm | 8000 ohm-cm | ASTM D257 |
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC1010 PPE+HIPS (Europe-Africa-Middle East) LNP* Stat-kon* HMC1010 compound is a 10% Carbon fiber reinforced. Static dissipative. Nonbrominated, nonchlornated flame retardant system. UL94 V-1 rated. |
|||
Volume Resistivity | 8000 ohm-cm | 8000 ohm-cm | ASTM D257 |
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC1010 PPE+PS LNP* Stat-kon* Noryl_HMC1010 compound is a 10% Carbon fiber reinforced. Static dissipative. Nonbrominated, nonchlor- nated flame retardant system. UL94 V-1 rated. |
|||
Volume Resistivity | 8000 ohm-cm | 8000 ohm-cm | ASTM D257 |
SABIC Innovative Plastics LNP STAT-KON Noryl_FMC1010 PPE+HIPS (Europe-Africa-Middle East) LNP* Stat-kon* Noryl_FMC1010 compound is a 10% carbon fiber, static dissipative, foamable resin Nonchlorinated, nonbrominated. UL94 V1 rated. Property values at 20% WR, 0.250"" wall. |
|||
Volume Resistivity | 8000 ohm-cm | 8000 ohm-cm | ASTM D257 |
SABIC Innovative Plastics LNP STAT-KON Noryl_FMC1010 PPE+PS LNP* Stat-kon* Noryl_FMC1010 compound is a 10% carbon fiber, static dissipative, foamable resin Nonchlorinated, nonbrominated. UL94 V1 rated. Property values at 20% WR, 0.250"" wall. |