Electrical Properties | Metric | English | Comments |
---|---|---|---|
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | per ASTM A596; heat treatment unknown |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Bar, Cold Drawn High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | per ASTM A596; heat treatment unknown |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Bar, Hydrogen Annealed at 2150°F (1177°C) High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | per ASTM A596, 0.025 - 0.125 in. thickness; heat treatment unknown |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Cold-Rolled High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | per ASTM A596, 0.014 in. thickness; heat treatment unknown |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Cold-Rolled High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | per ASTM A596, 0.025 - 0.125 in. thickness; heat treatment unknown |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Formed and Deep Draw Quality High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | per ASTM A596, 0.014 in. thickness; heat treatment unknown |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Formed and Deep Draw Quality High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | per ASTM A596; heat treatment unknown |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Bar, After Process Annealed at 1600°F (871°C) High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | per ASTM A596; heat treatment unknown |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Bar, Cold Drawn High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | per ASTM A596; heat treatment unknown |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Bar, Hydrogen Annealed at 2150°F (1177°C) High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | per ASTM A596, 0.025 - 0.125 in. thickness; heat treatment unknown |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Cold-Rolled High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | per ASTM A596, 0.014 in. thickness; heat treatment unknown |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Cold-Rolled High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | per ASTM A596, 0.025 - 0.125 in. thickness; heat treatment unknown |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Formed and Deep Draw Quality High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | per ASTM A596, 0.014 in. thickness; heat treatment unknown |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Strip, Formed and Deep Draw Quality High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | |
Alliance S-20A Samarium Cobalt Magnetic Material |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | |
Alliance S-20B Samarium Cobalt Magnetic Material |
|||
Magnetic Remanence, Br | 9000 - 9600 Gauss | 9000 - 9600 Gauss | |
Ceradyne SEMICORE® S2-17B MMPA 24/18 Sm2 (CoFeCuZr)17 Samarium Cobalt Magnet Magnetic alignment parallel to Compaction AxisApplications:Microwave amplifiers and oscillators for airborne equipmentTWT modules for phased array radarSmall motors for severe thermal conditions Her.. |
|||
Magnetic Remanence, Br | 9000 Gauss | 9000 Gauss | per ASTM A596; heat treatment unknown |
High Temp Metals Alloy 49 Iron-Nickel High Permeability Alloy, Bar, After Process Annealed at 1600°F (871°C) High Permeability "49" alloy is a 48% nickel-iron alloy which has a saturation flux density of approximately 15,000 Gauss after hydrogen annealing. Hysteresis loss is very low in either DC or AC cir.. |