Polymer Property : Dielectric Breakdown = 30000 V Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English	Comments
Dielectric Breakdown	>= 30000 V @Temperature 90.0 - 90.0 °C	>= 30000 V @Temperature 194 - 194 °F	Average value: 31500 V Grade Count:2
Overview of materials for Silicone, Molded, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Silicone, Molded, Glass Fiber Filled". Each property range of values reported is minimum and maximum val..
Dielectric Breakdown	>= 30000 V @Time 20.0 - 60.0 sec	>= 30000 V @Time 0.00556 - 0.0167 hour	Average value: 31500 V Grade Count:2
Overview of materials for Silicone, Molded, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Silicone, Molded, Glass Fiber Filled". Each property range of values reported is minimum and maximum val..
Dielectric Breakdown	30000 V @Thickness 1.57 mm	30000 V @Thickness 0.0620 in	Cond A; ASTM D229 S/S
Industrial Laminates/Norplex NP320 Cotton Fabric Description: Fine weave (less than 4 ounce/square yard) cotton fabric commonly called linen, combined with phenolic resin to provide better machining than NP310. For smaller and more intricate shape..
Dielectric Breakdown	>= 30000 V @Temperature 90.0 °C	>= 30000 V @Temperature 194 °F	In oil, parallel to laminations; IEC 1212-2 6.2
Hippe SI GC 201 Woven Glass Cloth Reinforced Silicone Resin - Sheet Used in electrical and electronic applications. Extremely good electrical properties under dry conditions; good properties under humid conditions.Information provided by Hippe.
Dielectric Breakdown	30000 V	30000 V	IPC TM-650 2.5.6
Arlon AD300C Commercial Microwave and RF Laminate Material Excellent Thermal Coefficient of Dielectric Constant (TCEr = -25 ppm/°C)Excellent PIM performanceHigh Thermal Conductivity ideal for Higher Power DesignsReduced Coefficient of Thermal Expansion in ..