Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English	Comments
Dielectric Breakdown	50000 V @Thickness 1.57 mm	50000 V @Thickness 0.0620 in	Condition A
Industrial Laminates/Norplex ES-1 Engraving Stock Description: Composed of white melamine paper core with various pigmented cover sheets.Thickness Tested: 0.0620â€, 0.125â€, and 0.500â€
Dielectric Breakdown	50000 V @Thickness 1.57 mm	50000 V @Thickness 0.0620 in	Condition A
Industrial Laminates/Norplex ES-2 Engraving Stock Description: Composed of black phenolic paper core, sub surfaces of white melamine, and various pigmented cover plies.
Dielectric Breakdown	50000 V @Thickness 1.57 mm	50000 V @Thickness 0.0620 in	Condition A
Industrial Laminates/Norplex ES-3 Engraving Stock Description: Contains black phenolic/paper core and various colored covers impregnated with melamine resin.
Dielectric Breakdown	50000 V @Thickness 1.57 mm	50000 V @Thickness 0.0620 in	Cond A; ASTM D229 S/S
Industrial Laminates/Norplex NP320E Cotton Fabric Description: Similar to NP320 with improved moisture resistance. Suitable for electrical applications in moderate humidity conditions.Thickness Tested: 0.062", 0.125", and 0.500â€
Dielectric Breakdown	50000 V @Thickness 1.57 mm	50000 V @Thickness 0.0620 in	Cond A; ASTM D229 S/S
Industrial Laminates/Norplex NP504 Glass Fabric Description: Woven glass fabric with high temperature phenolic resin. Good flexural, compressive and impact strengths at elevated temperatures. Capable of continuous operation at 175Â° C, see note..
Dielectric Breakdown	>= 50000 V @Temperature 90.0 °C, Time 20.0 sec	>= 50000 V @Temperature 194 °F, Time 0.00556 hour	Step -by-step test, In oil, parallel to laminations; IEC 1212-2 5.1
Hippe PF CP 22 Cellulose Paper Reinforced Phenolic Resin - Round, Rolled Tube High-voltage, electrical applications at power frequencies. High electric strength in oil.Information provided by Hippe.
Dielectric Breakdown	>= 50000 V @Temperature 90.0 °C, Time 60.0 sec	>= 50000 V @Temperature 194 °F, Time 0.0167 hour	Proof test, In oil, parallel to laminations; IEC 1212-2 5.1
Hippe PF CP 22 Cellulose Paper Reinforced Phenolic Resin - Round, Rolled Tube High-voltage, electrical applications at power frequencies. High electric strength in oil.Information provided by Hippe.