- Polymer Property : Electrical Resistivity = 0.0001164 ohm-cm
Polymer Property : Electrical Resistivity = 0.0001164 ohm-cm Product List
Electrical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, hot rolled and 1175°C solution annealed plate Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| Electrical Resistivity | 0.0001164 ohm-cm @Temperature 700 °C |
0.0001164 ohm-cm @Temperature 1290 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||