Polymer Property : Electrical Resistivity = 0.00000220 ohm-cm Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.00000220 ohm-cm	0.00000220 ohm-cm
OMG Americas GlidCop® AL-60 Dispersion Strengthened Copper GlidCop® AL-60 is copper that is dispersion strengthened with 1.1 wt% ultrafine particles of aluminum oxide. It is produced using an internal oxidation powder metallurgy process whereby aluminum o..
Electrical Resistivity	0.00000220 ohm-cm	0.00000220 ohm-cm
Lucas-Milhaupt BRAZE 720 Silver Based Cadmium Free Filler Metal Characteristics:Brazing 720 is the silver-copper eutectic composition and in melting it acts like a metallic element, i.e. it melts completely at a single temperature, thus it will quickly flow into..
Electrical Resistivity	0.00000220 ohm-cm	0.00000220 ohm-cm
Lucas-Milhaupt BRAZE 721 (VTG) Grade 1 Silver Based Cadmium Free Filler Metal Applications: Braze 721, a VTG version of Braze 720, is designed for all types of moderate temperature vacuum systems and particularly where maximum precautions must be taken to insure the presenc..
Electrical Resistivity	0.00000220 ohm-cm	0.00000220 ohm-cm
Lucas-Milhaupt BRAZE 721 (VTG) Grade 2 Silver Based Cadmium Free Filler Metal Applications: Braze 721, a VTG version of Braze 720, is designed for all types of moderate temperature vacuum systems and particularly where maximum precautions must be taken to insure the presenc..
Electrical Resistivity	0.00000220 ohm-cm	0.00000220 ohm-cm	80 % IACS
CMW® D50F Silver Nickel Alloy CMW® D50F can be fabricated into wire, rod and strip; however, the headability of CMW® D50F is limited to a narrow range. It is used for main contacts in circuit breakers and switching devices whe..
Electrical Resistivity	0.00000220 ohm-cm	0.00000220 ohm-cm	79 % IACS
CMW® ELKONIUM 46 Silver Alloy The alloying of small amounts of one of the precious metals, platinum, palladium or gold with silver increases the hardness, and reduces the metal transfer tendency. These alloys maintain a low cont..